Effect of trace Sc and Zr on aging behavior and tensile properties of2618alloy
来源期刊：中国有色金属学报(英文版)1999年第3期
论文作者：余琨 李松瑞 黎文献 肖于德
文章页码：593 - 598
Key words：scandium; zirconium; addition; 2618 alloy; tensile property
Abstract: The aging behavior of 2618 (Al-Cu-Mg-Fe-Ni) alloy added trace Sc and Zr was studied by Vicker’s hardness measurement at 200 and 300℃, and the tensile properties(yield strength, ultimate tensile strength and elongation) of alloys were measured at 20, 200, 250 and 300℃. The microstructures were observed by using optical microscope, SEM and TEM. It was found that the addition of Sc and Zr to 2618 alloy resulted in a uniform distribution of fine coherent Al3(Sc,Zr) precipitates which had obvious aging hardening effect and made the S’phase precipitate more homogeneously. The strength of alloy increased at ambient and elevated temperature without a decrease of ductility because of the precipitation strengthening and thermal stability of Al3(Sc,Zr) particles. The ductile fracture of alloy occurred by microviod nucleation, growth and coalescence, so the microvoid coalescence was the dominant fracture mechanism. Al3(Sc,Zr) particles could inhabit the recrystallization process of alloy 2618.