Martensitic transformation and magnetic properties of aged Ni-Fe-Ga-Ti shape memory alloy
来源期刊：International Journal of Minerals Metallurgy and Materials2013年第9期
论文作者：Nader El-Bagoury Mahmoud Mohamed Hessien
文章页码：867 - 873
摘 要：This article reports the efect of ageing on the microstructure,martensitic transformation,magnetic properties,and mechanical properties of Ni51Fe18Ga27Ti4shape memory alloy.There are fve specimens of this alloy aged at 573 up to 973 K for 3 h per each.This range of ageing temperature greatly afects the microstructure of the alloy.As the ageing temperature increased from 573 up to 973 K,the microstructure of Ni51Fe18Ga27Ti4alloy gradually changed from the entirely martensitic matrix at 573 K to the fully austenitic microstructure at 973 K.The volume fraction of precipitated Ni3Ti particles increased with the ageing temperature increasing from 573 to 773 K.Further increasing the ageing temperature to 973 K decreased the content of Ni3Ti in the microstructure.The martensitic transformation temperature was decreased steadily by increasing the ageing temperature.The magnetization saturation,remnant magnetization,and coercivity increased with the ageing temperature increasing up to 773 K.A further increase in ageing temperature decreased these magnetic properties.Moreover,the hardness values were gradually increased at frst by increasing the ageing temperature to 773 K,and then dramatically decreased to the lowest value at 973 K.
Nader El-Bagoury1,2，Mahmoud Mohamed Hessien1,2
2. Central Metallurgical Research and Development Institute (CMRDI), P.O. Box 87, Helwan, Cairo, Egypt
摘 要：This article reports the efect of ageing on the microstructure,martensitic transformation,magnetic properties,and mechanical properties of Ni51Fe18Ga27Ti4shape memory alloy.There are fve specimens of this alloy aged at 573 up to 973 K for 3 h per each.This range of ageing temperature greatly afects the microstructure of the alloy.As the ageing temperature increased from 573 up to 973 K,the microstructure of Ni51Fe18Ga27Ti4alloy gradually changed from the entirely martensitic matrix at 573 K to the fully austenitic microstructure at 973 K.The volume fraction of precipitated Ni3Ti particles increased with the ageing temperature increasing from 573 to 773 K.Further increasing the ageing temperature to 973 K decreased the content of Ni3Ti in the microstructure.The martensitic transformation temperature was decreased steadily by increasing the ageing temperature.The magnetization saturation,remnant magnetization,and coercivity increased with the ageing temperature increasing up to 773 K.A further increase in ageing temperature decreased these magnetic properties.Moreover,the hardness values were gradually increased at frst by increasing the ageing temperature to 773 K,and then dramatically decreased to the lowest value at 973 K.
关键词：