HIC and SSC Behavior of High-Strength Pipeline Steels
来源期刊：Acta Metallurgica Sinica2015年第7期
论文作者：Xian-Bo Shi Wei Yan Wei Wang Lian-Yu Zhao Yi-Yin Shan Ke Yang
文章页码：799 - 808
摘 要：In this study,hydrogen-induced cracking（HIC） and sulfide stress corrosion cracking（SSC） behaviors of highstrength pipeline steels in four different strength grades（X70,X80,X90 and X100） with the microstructure of acicular ferrite were estimated.The results showed that both of X70 and X80 steels exhibited better HIC resistance,and their susceptibility to HIC increased with the strength grade.HIC parameters,including cracking length ratio,cracking thickness ratio（CTR） and cracking sensitivity ratio,were all increased,and among these,the CTR increased most,with the increase in the strength grade.HIC was found to initiate and grow along the hard boundaries such as large size martensite/austenite（M/A） islands and bainitic ferrite.In addition,the density of hydrogen-induced blister on the steel surface was increased with the decrease in p H value for the same-grade pipeline steels.SSC susceptibilities of X80,X90 and X90-C were revealed to subsequently decrease,which was related to the large size M/A islands.
Xian-Bo Shi1,2，Wei Yan1，Wei Wang1，Lian-Yu Zhao3，Yi-Yin Shan1，Ke Yang1
1. Institute of Metal Research,Chinese Academy of Sciences2. University of Chinese Academy of Sciences3. Petro China Pipeline Company
摘 要：In this study,hydrogen-induced cracking（HIC） and sulfide stress corrosion cracking（SSC） behaviors of highstrength pipeline steels in four different strength grades（X70,X80,X90 and X100） with the microstructure of acicular ferrite were estimated.The results showed that both of X70 and X80 steels exhibited better HIC resistance,and their susceptibility to HIC increased with the strength grade.HIC parameters,including cracking length ratio,cracking thickness ratio（CTR） and cracking sensitivity ratio,were all increased,and among these,the CTR increased most,with the increase in the strength grade.HIC was found to initiate and grow along the hard boundaries such as large size martensite/austenite（M/A） islands and bainitic ferrite.In addition,the density of hydrogen-induced blister on the steel surface was increased with the decrease in p H value for the same-grade pipeline steels.SSC susceptibilities of X80,X90 and X90-C were revealed to subsequently decrease,which was related to the large size M/A islands.
关键词：