两流板坯连铸中间包控流装置的优化

来源期刊:钢铁钒钛2010年第3期

论文作者:李娇 李京社 杨树峰 孙丽媛 林晓川 白瑞国

文章页码:44 - 49

关键词:板坯连铸; 中间包; 挡墙; 挡坝; 水模拟

Key words:slab continuous casting; tundish; weir; dam; water model

摘    要:在相似理论的基础上,按照1∶3的比例建立了"两流板坯连铸中间包"水力学模型,通过挡墙与挡坝不同高度及位置的组合来优化中间包的内部结构并确定出最佳设计方案。试验结果表明:优化后能将原型中间包的滞止时间由83s延长到97s,平均停留时间由296s延长到432s,死区由46%减小到21%,电导率微观波动值由0.04ms/cm降低到0.025ms/cm以内。

Abstract: Based on the similar theory,water model of two strand slab continuous casting tundish was established in the ratio of 1∶3.The inner structure of tundish is optimized by the combination of weirs and dams with different heights and positions.The experiment results show that the minimum residence time in the modified tundish increases from 83 s to 97 s,the mean residence time increases from 296 s to 432 s,the dead zone volume decreases from 46% to 21% and all the microscopic fluctuations decrease from 0.04 ms/cm to 0.025 ms/cm,the goal of optimizing the inner structure of the tundish has been achieved.

详情信息展示

两流板坯连铸中间包控流装置的优化

李娇1,李京社1,杨树峰2,孙丽媛2,林晓川0,白瑞国2

(1.北京市北京科技大学 冶金与生态工程学院
2.北京科技大学 冶金与生态学院,北京 100083)

摘 要:在相似理论的基础上,按照1∶3的比例建立了"两流板坯连铸中间包"水力学模型,通过挡墙与挡坝不同高度及位置的组合来优化中间包的内部结构并确定出最佳设计方案。试验结果表明:优化后能将原型中间包的滞止时间由83s延长到97s,平均停留时间由296s延长到432s,死区由46%减小到21%,电导率微观波动值由0.04ms/cm降低到0.025ms/cm以内。

关键词:板坯连铸; 中间包; 挡墙; 挡坝; 水模拟

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号