Preparation of Well Dispersed and Ultra-Fine Ce(Zr)O2 Mixed Oxide by Mechanochemical Processing
来源期刊：JOURNAL OF RARE EARTHS2004年第6期
论文作者：陈伟凡 李永绣 程昌明 周雪珍
Key words：ceria-zirconia mixed oxide; ultra-fine powders; mechanochemical process; rare earths;
Abstract: Ultra-fine CeO2-ZrO2 mixed oxide was successfully synthesized by wet-solid phase mechanochemical processing, Ce2(CO3)3·8H2O, ZrOCl2·xH2O and ammonia were used as reactants. It is found that the crystalline Ce2(CO3)3·8H2O and ZrOCl2·xH2O are changed to amorphous cerium and zirconium hydroxide precursor after milling with ammonia, and Ce0.15Zr0.85O2 mixed oxide with pure tetragonal phase structure and medium particle size(D50)less than 1μm is formed by calcining precursor over 673 K. The XRD patterns indicate that the crystal unite size increases with rising calcining temperature due to crystal growth. However, the particle size and BET surface area of the Ce(Zr)O2 mixed oxide decreases with rising calcining temperature, which may be attributed to the contract of particles and the vanish of holes inside grains.
陈伟凡1，李永绣1，程昌明1，周雪珍1
(1.Rare Earth Technology Research Center, Nanchang Univeisity, Nanchang 330047, China)
Abstract:Ultra-fine CeO2-ZrO2 mixed oxide was successfully synthesized by wet-solid phase mechanochemical processing, Ce2(CO3)3·8H2O, ZrOCl2·xH2O and ammonia were used as reactants. It is found that the crystalline Ce2(CO3)3·8H2O and ZrOCl2·xH2O are changed to amorphous cerium and zirconium hydroxide precursor after milling with ammonia, and Ce0.15Zr0.85O2 mixed oxide with pure tetragonal phase structure and medium particle size(D50)less than 1μm is formed by calcining precursor over 673 K. The XRD patterns indicate that the crystal unite size increases with rising calcining temperature due to crystal growth. However, the particle size and BET surface area of the Ce(Zr)O2 mixed oxide decreases with rising calcining temperature, which may be attributed to the contract of particles and the vanish of holes inside grains.
Key words:ceria-zirconia mixed oxide; ultra-fine powders; mechanochemical process; rare earths;
【全文内容正在添加中】