Fabrication and Magnetic Properties of Composite Ni0.5Zn0.5Fe2O4/Pb(Zr0.52Ti0.48)O3 Nanofibers by Electrospinning
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2011年第3期
论文作者：沈湘黔
文章页码：384 - 387
摘 要：One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT） nanofibers with average diameters about 65 nm are prepared by electrospinning from poly（vinyl pyrrolidone） （PVP） and metal salts.The precursor composite NZFO/PZT/PVP nanofibers and the subsequent calcined NZFO/PZT nanofibers are investigated by Fourier transform infrared spectroscopy （FT- IR） ,X-ray diffraction （XRD）,scanning electron microscopy （SEM）.The magnetic properties for nanofibers are measured by vibrating sample magnetometer（VSM）.The NZFO/PZT nanofibers obtained at calcination temperature of 900 °C for 2 h consist of the ferromagnetic spinel NZFO and ferroelectric perovskite PZT phases,which are constructed from about 37 nm NZFO and 17 nm PZT grains.The saturation magnetization of these NZFO/PZT nanofibers increases with increasing calcination temperature and contents of NZFO in the composite.
沈湘黔
School of Materials Science and Engineering,Jiangsu University
摘 要：One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT） nanofibers with average diameters about 65 nm are prepared by electrospinning from poly（vinyl pyrrolidone） （PVP） and metal salts.The precursor composite NZFO/PZT/PVP nanofibers and the subsequent calcined NZFO/PZT nanofibers are investigated by Fourier transform infrared spectroscopy （FT- IR） ,X-ray diffraction （XRD）,scanning electron microscopy （SEM）.The magnetic properties for nanofibers are measured by vibrating sample magnetometer（VSM）.The NZFO/PZT nanofibers obtained at calcination temperature of 900 °C for 2 h consist of the ferromagnetic spinel NZFO and ferroelectric perovskite PZT phases,which are constructed from about 37 nm NZFO and 17 nm PZT grains.The saturation magnetization of these NZFO/PZT nanofibers increases with increasing calcination temperature and contents of NZFO in the composite.
关键词：