Sn对镁合金显微组织和力学性能的影响
来源期刊：中国有色金属学报1999年第1期
论文作者：孙扬善 翁坤忠 袁广银
文章页码：55 - 60
关键词：镁合金，锡，力学性能
Key words：magnesium alloy, Sn, mechanical property
摘 要：研究了Sn对镁合金显微组织和力学性能的影响。 研究结果表明， 纯镁中加入Sn后能使纯镁铸锭中粗大的柱状晶转化为均匀的等轴晶， 并有效地细化晶粒， 同时在显微组织中形成具有立方C1结构的Mg2Sn颗粒相。 由于Mg2Sn颗粒相显微硬度和熔点高， 热稳定性好， 因而对基体具有有效的弥散强化作用， 提高了Mg-Sn二元合金的室温及高温强度。 在Mg-9Al-0.8Zn基合金中加入少量的Sn便能有效地提高合金的耐热性， 而加入过多的Sn反而会导致合金高温强度下降。
Abstract: Effects of Sn addition on the microstructure and mechanical properties of magnesium alloys were studied. Results showed that the Sn addition to magnesium modifies the microstructure of magnesium ingot and causes the formation of Mg2Sn precipitates with C1 cubic structure. The strength of Mg-Sn alloy has increased at both ambient and elevated temperatures due to the high micro-hardness and melting point as well as the high thermal stability of the precipitates. In the ternary alloy of Mg-9Al-0.8Zn small amount addition of Sn results in significant improvement of heatresistance. However, the excessive Sn addition to Mg-9Al-0.8Zn leads to the decrease of the strength at elevated temperature.