Cu Partitioning Behavior and Its Effect on Microstructure and Mechanical Properties of 0.12C-1.33Mn-0.55Cu Q&P Steel
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2017年第5期
论文作者：陈连生 HU Baojia 郭士永 田亚强 ZHENG Xiaoping SONG Jinying XU Yong
文章页码：1179 - 1185
摘 要：Cu, as an austenitic stable element, is added to steel in order to suppress the adverse effects of high content of C and Mn on welding. Based on C partitioning, Cu and Mn partitioning can further improve the stability of retained austenite in the intercritical annealing process. A sample of low carbon steel containing Cu was treated by the intercritical annealing, then quenching process(I&Q). Subsequently, another sample was treated by the intercritical annealing, subsequent austenitizing, then quenching and partitioning process(I&Q&P). The effects of element partitioning behavior in intercritical region on the microstructure and mechanical properties of the steel were studied. The results showed that after the I&Q process ferrite and martensite could be obtained, with C, Cu and Mn enriched in the martensite. When intercritically heated at 800 ℃, Cu and Mn were partitioned from ferrite to austenite, which was enhanced gradually as the heating time was increased. This partitioning effect was the most obvious when the sample was heated at 800 ℃ for 40 min. At the early stage of α→γ transformation, the formation of γ was controlled by the partitioning of carbon, while at the later stage, it was mainly affected by the partitioning of Cu and Mn. After the I&Q&P process, the partitioning effect of Cu and Mn element could be retained. C was assembled in retained austenite during the quenching and partitioning process. The strength and elongation of I&Q&P steel was increased by 5 305 MPa% compared with that subjected to Q&P process. The volume fraction of retained autensite was increased from 8.5% to 11.2%. Hence, the content of retained austenite could be improved significantly by Mn and Cu partitioning, which increased the elongation of steel.
陈连生1，HU Baojia1，XU Jinghui1，田亚强1，ZHENG Xiaoping1，SONG Jinying1，XU Yong2
1. Hebei Key Laboratory of Modern Metallurgy Technology, North China University of Science and Technology2. Institute of Metal Research, Chinese Academy of Sciences
摘 要：Cu, as an austenitic stable element, is added to steel in order to suppress the adverse effects of high content of C and Mn on welding. Based on C partitioning, Cu and Mn partitioning can further improve the stability of retained austenite in the intercritical annealing process. A sample of low carbon steel containing Cu was treated by the intercritical annealing, then quenching process(I&Q). Subsequently, another sample was treated by the intercritical annealing, subsequent austenitizing, then quenching and partitioning process(I&Q&P). The effects of element partitioning behavior in intercritical region on the microstructure and mechanical properties of the steel were studied. The results showed that after the I&Q process ferrite and martensite could be obtained, with C, Cu and Mn enriched in the martensite. When intercritically heated at 800 ℃, Cu and Mn were partitioned from ferrite to austenite, which was enhanced gradually as the heating time was increased. This partitioning effect was the most obvious when the sample was heated at 800 ℃ for 40 min. At the early stage of α→γ transformation, the formation of γ was controlled by the partitioning of carbon, while at the later stage, it was mainly affected by the partitioning of Cu and Mn. After the I&Q&P process, the partitioning effect of Cu and Mn element could be retained. C was assembled in retained austenite during the quenching and partitioning process. The strength and elongation of I&Q&P steel was increased by 5 305 MPa% compared with that subjected to Q&P process. The volume fraction of retained autensite was increased from 8.5% to 11.2%. Hence, the content of retained austenite could be improved significantly by Mn and Cu partitioning, which increased the elongation of steel.
关键词：