Electroplating of Zr-Ti Alloy
来源期刊：Rare Metals1989年第3期
论文作者：Ye Shangyun Li Guoxun General Research Institute for Non-ferrous Metals,Beijing
文章页码：1 - 5
摘 要：<正> The electrodeposition of Zr-Ti alloy has been studied in molten fluoride system consisting of fluorides of both zirconium andtitanium dissolved in FLINAK（KF:NaF:LiF=42.0:11.5:46.5 mol）.A coherent dense deposit of the alloy with a smooth sur-face is obtained on different material substrates.X-ray diffraction has demonstrated that the alloy deposit is a Ti-Zr solid solu-tion with Ti mainly and its preferred orientation is strongly along Ti[110]direction.The properties of the deposit are better thanthose of a pure zirconium coating.The optimum operating parameters are a temperature of about 800℃,a current density lessthan 40mA/cm2,a solution about 15wt% ZrF4 and 15wt% K2TiF6.in FLINAK as well as pure zirconium as anode material.
摘要：<正> The electrodeposition of Zr-Ti alloy has been studied in molten fluoride system consisting of fluorides of both zirconium andtitanium dissolved in FLINAK（KF:NaF:LiF=42.0:11.5:46.5 mol）.A coherent dense deposit of the alloy with a smooth sur-face is obtained on different material substrates.X-ray diffraction has demonstrated that the alloy deposit is a Ti-Zr solid solu-tion with Ti mainly and its preferred orientation is strongly along Ti[110]direction.The properties of the deposit are better thanthose of a pure zirconium coating.The optimum operating parameters are a temperature of about 800℃,a current density lessthan 40mA/cm2,a solution about 15wt% ZrF4 and 15wt% K2TiF6.in FLINAK as well as pure zirconium as anode material.
关键词：