Synthesis and luminescence characteristics of terbium（Ⅲ） activated NaSrBO3
来源期刊：Journal of Rare Earths2012年第9期
论文作者：P.A. Nagpure S.K. Omanwar
文章页码：856 - 859
摘 要：The thermoluminescence （TL） and photoluminescence （PL） properties of the phosphor NaSrBO 3 :Tb 3+ were reported and discussed. The combustion technique was used for the synthesis of polycrystalline samples of NaSrBO 3 :Tb 3+ . The TL glow curve of the compound had a simple structure with a single peak at 434 K. TL sensitivity of the phosphor was found to be more than that of （LiF:Mg,Cu,P）. The TL glow curve was studied as a function of concentration of dopant and dose of gamma ray irradiation. The kinetic parameters of the thermoluminescence of NaSrBO 3 : Tb 3+ were calculated employing the peak shape method. The photoluminescence （PL） properties of Tb 3+ doped in NaSrBO 3 were studied over the 200-400 nm excitation range. The excitation spectra of NaSrBO 3 :Tb 3+ consisted of single narrow band peaking at about 236 nm. The emission spectra monitored at 236 nm excitation consisted of a series of sharp lines peaking at 489, 544, 586 and 622 nm corresponding to the 5 D 4 → 7 F j （j=3,4,5,6） transitions within the 4f 8 configurations of Tb 3+ .
P.A. Nagpure，S.K. Omanwar
Department of Physics, SGB Amravati University, Amravati-444602 (M.S.), India
摘 要：The thermoluminescence （TL） and photoluminescence （PL） properties of the phosphor NaSrBO 3 :Tb 3+ were reported and discussed. The combustion technique was used for the synthesis of polycrystalline samples of NaSrBO 3 :Tb 3+ . The TL glow curve of the compound had a simple structure with a single peak at 434 K. TL sensitivity of the phosphor was found to be more than that of （LiF:Mg,Cu,P）. The TL glow curve was studied as a function of concentration of dopant and dose of gamma ray irradiation. The kinetic parameters of the thermoluminescence of NaSrBO 3 : Tb 3+ were calculated employing the peak shape method. The photoluminescence （PL） properties of Tb 3+ doped in NaSrBO 3 were studied over the 200-400 nm excitation range. The excitation spectra of NaSrBO 3 :Tb 3+ consisted of single narrow band peaking at about 236 nm. The emission spectra monitored at 236 nm excitation consisted of a series of sharp lines peaking at 489, 544, 586 and 622 nm corresponding to the 5 D 4 → 7 F j （j=3,4,5,6） transitions within the 4f 8 configurations of Tb 3+ .
关键词：