Hot deformation behavior of microstructural constituents in a duplex stainless steel during high-temperature straining

来源期刊:International Journal of Minerals Metallurgy and Materials2013年第10期

论文作者:Amir Momeni Shahab Kazemi Ali Bahrani

文章页码:953 - 960

摘    要:The hot deformation characteristics of 1.4462 duplex stainless steel(DSS)were analyzed by considering strain partitioning between austenite and ferrite constituents.The individual behavior of ferrite and austenite in microstructure was studied in an iso-stress condition.Hot compression tests were performed at temperatures of 800-1100 C and strain rates of 0.001-1 s 1.The flow stress was modeled by a hyperbolic sine constitutive equation,the corresponding constants and apparent activation energies were determined for the studied alloys.The constitutive equation and law of mixture were used to measure the contribution factor of each phase at any given strain.It is found that the contribution factor of ferrite exponentially declines as the Zener-Hollomon parameter(Z)increases.On the contrary,the austenite contribution polynomially increases with the increase of Z.At low Z values below 2.6.×1015(lnZ=35.5),a negative contribution factor is determined for austenite that is attributed to dynamic recrystallization.At high Z values,the contribution factor of austenite is about two orders of magnitude greater than that of ferrite,and therefore,austenite can accommodate more strain.Microstructural characterization via electron back-scattered difraction(EBSD)confirms the mechanical results and shows that austenite recrystallization is possible only at high temperature and low strain rate.

详情信息展示

Hot deformation behavior of microstructural constituents in a duplex stainless steel during high-temperature straining

Amir Momeni1,Shahab Kazemi2,Ali Bahrani1

1. Materials Science and Engineering Department,Hamedan University of Technology2. Department of Materials Engineering,Faculty of Engineering,Bu Ali Sina University

摘 要:The hot deformation characteristics of 1.4462 duplex stainless steel(DSS)were analyzed by considering strain partitioning between austenite and ferrite constituents.The individual behavior of ferrite and austenite in microstructure was studied in an iso-stress condition.Hot compression tests were performed at temperatures of 800-1100 C and strain rates of 0.001-1 s 1.The flow stress was modeled by a hyperbolic sine constitutive equation,the corresponding constants and apparent activation energies were determined for the studied alloys.The constitutive equation and law of mixture were used to measure the contribution factor of each phase at any given strain.It is found that the contribution factor of ferrite exponentially declines as the Zener-Hollomon parameter(Z)increases.On the contrary,the austenite contribution polynomially increases with the increase of Z.At low Z values below 2.6.×1015(lnZ=35.5),a negative contribution factor is determined for austenite that is attributed to dynamic recrystallization.At high Z values,the contribution factor of austenite is about two orders of magnitude greater than that of ferrite,and therefore,austenite can accommodate more strain.Microstructural characterization via electron back-scattered difraction(EBSD)confirms the mechanical results and shows that austenite recrystallization is possible only at high temperature and low strain rate.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号