Mechanical Properties and Microstructure Evolution of AA1100 Aluminum Sheet Processed by Accumulative Press Bonding Process
来源期刊：Acta Metallurgica Sinica2016年第8期
论文作者：Amir Mostafapor Vahid Mohammadinia
文章页码：735 - 741
摘 要：Accumulative press bonding（APB） is a novel variant of severe plastic deformation processes,which is devised to produce materials with ultra-fine grain.In the present work,the mechanical properties and microstructural evolution of AA1100 alloy,which is produced by APB technique,were investigated.The study of the microstructure of AA1100 alloy was performed by optical microscopy.The results revealed that the grain size of the samples decreased to 950 nm after six passes of APB process.The yield strength of AA1100 alloy after six passes of the process increased up to 264 MPa,which is three times higher than that of the as-cast material（89 MPa）.After six passes,microhardness values of AA1100 alloy increased from 38 to 61 HV.Furthermore,the results showed that the behavior of variations in mechanical properties is in accordance with the microstructural changes and it can be justified by using the Hall-Patch equation.Moreover,the rise in the yield strength can be attributed to the reduction in the grain size leading to the strain hardening.
Amir Mostafapor1，Vahid Mohammadinia2
1. Department of Mechanical Engineering,University of Tabriz2. Department of Mechanical Engineering,University of Maragheh
摘 要：Accumulative press bonding（APB） is a novel variant of severe plastic deformation processes,which is devised to produce materials with ultra-fine grain.In the present work,the mechanical properties and microstructural evolution of AA1100 alloy,which is produced by APB technique,were investigated.The study of the microstructure of AA1100 alloy was performed by optical microscopy.The results revealed that the grain size of the samples decreased to 950 nm after six passes of APB process.The yield strength of AA1100 alloy after six passes of the process increased up to 264 MPa,which is three times higher than that of the as-cast material（89 MPa）.After six passes,microhardness values of AA1100 alloy increased from 38 to 61 HV.Furthermore,the results showed that the behavior of variations in mechanical properties is in accordance with the microstructural changes and it can be justified by using the Hall-Patch equation.Moreover,the rise in the yield strength can be attributed to the reduction in the grain size leading to the strain hardening.
关键词：