High temperature oxidation behavior of Ni-based superalloy GH586 in air

来源期刊：Rare Metals2017年第11期

论文作者：Jiang-Dong Cao Jun-Song Zhang Yin-Qun Hua Zhen Rong Rui-Fang Chen Yun-Xia Ye

文章页码：878 - 885

摘要：In this paper, the isothermal oxidation kinetics and oxidation behavior of GH586 superalloy from 800 to 1000 ℃ were investigated. The oxide scale morphologies of the surfaces and the cross sections after oxidation were characterized by means of X-ray diffraction（XRD） and scanning electron microscope（SEM） equipped with energy-dispersive spectroscopy（EDS）. The results show that the growth of the oxide scales on the surface of superalloy GH586 obeys a parabolic law with the activation energy of 241.4 kJ mol^-1 from 800 to 1000 ℃. The dense oxide scale formed at 800 ℃ is mainly composed of Cr₂O₃, NiCr₂O₄ and a small amount of TiO₂. At 900 ℃,the oxide scale is divided into two layers: the outer layer with multiple cracks is mainly composed of Cr₂O₃ and Ti0₂, while the inner is a layer of dense Cr₂O₃. Under the oxide scale, aluminum-rich oxides along the grain boundaries are generated by the internal oxidation. At 1000 ℃for 100 h, cracks throughout the whole oxide film accelerate the oxidation rate of Ni-based superalloy GH586 and large blocks of TiO₂ in the oxide scale are generated,resulting in the spallation of oxide scale.

稀有金属(英文版) 2017,36(11),878-885

High temperature oxidation behavior of Ni-based superalloy GH586 in air

Jiang-Dong Cao Jun-Song Zhang Yin-Qun Hua Zhen Rong Rui-Fang Chen Yun-Xia Ye

School of Material Science and Engineering, Jiangsu University

Mechanical and Electrical Department, Nantong Shipping College

School of Mechanical Engineering, Jiangsu University

收稿日期：5 November 2015

基金：financially supported by the National Natural Science Foundation of China (No.51641102);the Natural Science Foundation of Jiangsu Province (No.16KJB430035);the Nantong Science and Technology Project (No. GY12015032);

High temperature oxidation behavior of Ni-based superalloy GH586 in air

Jiang-Dong Cao Jun-Song Zhang Yin-Qun Hua Zhen Rong Rui-Fang Chen Yun-Xia Ye

School of Material Science and Engineering, Jiangsu University

Mechanical and Electrical Department, Nantong Shipping College

School of Mechanical Engineering, Jiangsu University

Abstract：

In this paper, the isothermal oxidation kinetics and oxidation behavior of GH586 superalloy from 800 to 1000 ℃ were investigated. The oxide scale morphologies of the surfaces and the cross sections after oxidation were characterized by means of X-ray diffraction(XRD) and scanning electron microscope(SEM) equipped with energy-dispersive spectroscopy(EDS). The results show that the growth of the oxide scales on the surface of superalloy GH586 obeys a parabolic law with the activation energy of 241.4 kJ mol^-1 from 800 to 1000 ℃. The dense oxide scale formed at 800 ℃ is mainly composed of Cr₂O₃, NiCr₂O₄ and a small amount of TiO₂. At 900 ℃,the oxide scale is pided into two layers: the outer layer with multiple cracks is mainly composed of Cr₂O₃ and Ti0₂, while the inner is a layer of dense Cr₂O₃. Under the oxide scale, aluminum-rich oxides along the grain boundaries are generated by the internal oxidation. At 1000 ℃for 100 h, cracks throughout the whole oxide film accelerate the oxidation rate of Ni-based superalloy GH586 and large blocks of TiO₂ in the oxide scale are generated,resulting in the spallation of oxide scale.

Keyword：

Ni-based superalloy; Internal oxidation; High temperature oxidation behavior; Oxidation kinetics;

Author： Yin-Qun Hua e-mail:huayq@ujs.edu.cn;

Received： 5 November 2015

1 Introduction

Superalloys have been widely used in high temperature environments,such as aircraft engine blades,nuclear energy equipment and the petroleum industry,due to its excellent resistance to hot corrosion [ 1] ,fatigue [ 2] and oxidation [ 3, 4] at high temperatures.Among the various superalloy systems,Ni-based superalloys have good comprehensive properties,so they are widely used in a variety of high performance engine parts [ 5, 6, 7] .Ni-based superalloy GH586,when developed successfully,can serve between 750 and 850℃ [ 8] .It is often used in engine turbine disks of lox or kerosene rockets and the first stage turbine rotors of several new intercontinental missiles in China [ 9] .

Oxidation resistance of superalloys depends on dense oxidation films on the surface of materials,which grow slowly and prevent oxygen from diffusing to the matrix [ 10] .It is well known that Al₂O₃,Cr₂O₃ and SiO₂ films with good thermodynamics stability at high temperatures are generated in the process of superalloys oxidation [ 11] .Owing to the different content of elements,the preparation process and chemical composition in superalloys,the oxidation behaviors of the superalloys are quite different.It is reported that the oxidation behaviors of superalloys were investigated by many scholars,such as Inconel 713 [ 12] ,MAR-M247 [ 13] ,DZ40 M [ 14] and GTD-111 [ 15] .According to these studies,whatever oxide films of superalloys will gradually spall with the increase of working temperature and time,this results in accelerating oxidation corrosion rate of superalloys significantly.In order to find out the reasons for spallation of oxide scales,many researchers carried out plenty of work.It is well accepted that internal oxidation will take place to form the acicular morphology inner oxides during high temperature oxidation,which may be the initiation sites of cracks that result in the destruction of the oxide films with temperature and time increasing [ 16, 17] .Some elements in Ni-based super alloys,such as sulfur,carbon,titanium,etc.,may form the corresponding compounds in grain boundaries [ 18, 19] ,the size of which can become larger with temperatures increasing,reducing the bonding strength between oxide scales and the matrix and destroying the continuity of oxidation films [ 20, 21] .Although the oxidation behaviors of a few superalloys were investigated,there are very few literatures on oxidation resistance of Nibased superalloy GH586,and the further study on oxidation mechanism is needed.

In this paper,the high temperature oxidation behavior of Ni-based superalloy GH586 at 800,900 and 1000℃was investigated.The oxidation kinetics,the oxide scale composition,the surface and cross-sectional morphologies were elaborated.The growth and spallation mechanism of oxidation scales were revealed,providing a theoretical basis for practical engineering applications and failure analyses.

2 Experimental

2.1 Materials

The alloy used in this experiment was Ni-based superalloy GH586 (nominal composition:19.00 wt%Cr,11.00 wt%Co,1.60 wt%Al,3.20 wt%Ti,8.00 wt%Mo,3.00 wt%W,0.06 wt%C,balanced Ni).It was dealt with precipitation strengthening and aging treatment.Figure 1 shows the microstructure of the superalloy GH586.From Fig.1a,it can be seen that the superalloy grains have a fine equiaxed structure and distribute uniformly.According to Fig.1d,e,the white chains in grain boundaries and blocks in grain interior in Fig.1b are carbides,and they are respectively M₂₃C₆ and M₆C [ 8] .γ’phase which is the main strengthening phase in the alloy in Fig.lc is almost50-60 nm in size,and the morphologies seem approximately cuboid [ 13] .

2.2 Oxidation experiments

Rectangular specimens with dimensions of10 mm×10 mm×5 mm were cut from Ni-based superalloy GH586 by electrical discharge machining (EDM).The surfaces of these specimens were ground to 1200 mesh with SiC sandpaper and polished before examination.The continuous-isothermal-mass-change measurements were performed from 800 to 1000℃in air for 100 h.The specimens were suspended in a thermo balance with a Pt wire.

Fig.1 SEM images of GH586 superalloy at room temperature:a metallographical structure,b carbides,and cγ'phase;EDS analysis of carbides:d M₂₃C₆ and e M₆C

Fig.2 Square of weight gain per unit area (△m²) versus time for Ni-based superalloy GH586 oxidized at temperature ranging from 800 to1000℃a and temperature dependence of parabolic rate constant for oxidation of Ni-based superalloy GH586 b

2.3 Microstructural analysis of oxide scale

After oxidation,the specimens were characterized.The phase composition of the oxide scale was measured by X-ray diffractometer (XRD,D8 Advance) with copper target at 3 kW in 2θrange of 10°-90°.The surface morphology and chemical composition of the oxide scale were investigated by scanning electron microscopy (SEM,JSM-7001F) equipped with an energy dispersive spectroscopy(EDS) system.

3 Results and discussion

3.1 Oxidation kinetic s

Figure 2 shows the square of weight gain per unit area(Δm²) as a function of time in the temperature range of800-1000℃in air.After oxidation at 900℃for 100 h and 1000℃for 50 h,the oxide scales on the surface just begin to spall.From the linear fit in Fig.2a,it can be concluded that the oxidation of Ni-based superalloy GH586from 800 to1000℃is in excellent agreement with a parabolic rate law.The parabolic rate constant (K_p)increases from 1.44×10^-5 mg²·cm^-4.s^-1 at 800℃to4.81×10^-5 mg².cm^-4·s^-1 at 1000℃.

The following equation indicates the temperature dependence of the parabolic rate constants.

where Q denotes oxidation activation energy which is energy barrier crossed during oxidation,K₀ is a constant which can be obtained by solving equations,R is gas constant and T is temperature.According to the fitted line,the oxidation activation energy of Ni-based superalloy GH586 is 241.4 kJ·mol^-1 from 800 to 1000℃,as shown in Fig.2b.It is close to the diffusion activation(259 kJ·mol^-1) of Cr³⁺in oxide scale [ 22] ,indicating that the oxidation behaviors of superalloy GH586 are controlled by the diffusion of Cr³⁺in oxide scale.It is almost in accordance with that of Ni-based superalloy K44 reported in Ref. [ 22] .

3.2 Composition of oxide scale

Figure 3 shows XRD patterns of oxide scales of GH586superalloy oxidized at 800,900 and 1000℃for 100 h.After oxidation at 800,900 and 1000℃for 100 h,the compositions of oxide scale on the surface are basically the same,but the relative content of each constituent phase changes.The oxide films at different temperatures consist of Cr₂O₃,spinels NiCr₂O₄ and TiO₂.The diffraction peak of the matrix is stronger after oxidation at 800℃for100 h,illustrating that the formed oxide film is thin.The base peak becomes weaker and the thickness of oxide film increases with temperature increasing.The peak of TiO₂ is not obvious,while Cr₂O₃ and NiCr₂O₄ peaks are relatively strong.It is shown that the film formed at 800℃is mainly composed of Cr₂O₃,NiCr₂O₄ and a small amount of TiO₂.At 900℃,the peaks of all the constituent phases in the film are significantly enhanced,and the TiO₂ peak is strong.When the temperature rises to 900℃,Cr₂O₃ and NiCr₂O₄ in oxide film form a thicker oxide film which contains a large amount of TiO₂.The titanium oxide coarsens and makes the oxide scale loose,reducing the density of the outer layer of oxide film at the initial stage of oxidation [ 14] .The weak TiO₂ peak at 1000℃is caused by the peeling of the bulk pre-formed TiO₂ oxidation layer,and the inner Cr₂O₃ is exposed,resulting in further oxidation of the alloy.Moreover,there are a small amount of NiCr₂O₄ oxides which would consume a little Cr element that can be supplied to oxide scale with temperature1ncreas1ng.

Fig.3 XRD patterns of oxide surfaces on Ni-based superalloy GH586 samples oxidized from 800 to 1000℃for 100 h

3.3 Surface and cross-sectional morphology of oxide scale

Figure 4a-c shows surface morphologies of oxide scale at800,900 and 1000℃,respectively.Different surface morphologies could be observed,and the grain size of the oxides increases with temperature increasing.A dense oxide scale with well-shaped crystallites is observed for the sample oxidized at 800℃.EDS and XRD analyses show that the oxide is mainly composed of Cr₂O₃,TiO₂ and NiCr₂O₄.As shown in Fig.4a,the small white oxide is TiO₂.Ti content of oxide scale at 900℃for 100 h is more than that at 800℃for 100 h (Fig.4d,e),meanwhile,Cr content decreases obviously.These titanium oxides would agglomerate into coarse particles with time gradually increasing,which makes the outer oxide film loose and provides the channel for oxygen diffusing into substrate.In Fig.4c,f,it is found that a lot of holes in outer oxide film are formed and Ti content was decreases greatly,which results from the large oxide scale spalled.With time increasing at 1000℃,TiO₂ forms large particles and destroys the continuity of the oxide film;moreover,the spinels NiCr₂O₄ generated in the process of oxidation consume a great quantity of Cr elements in oxide film,leading to less Cr₂O₃ than that at 900℃.In addition,from Fig.4d-f,it can be seen that a small amount of aluminum oxides in oxidation scales are found,and Al content is almost unchanged.Owing to its low content,a dense and continuous aluminum oxide scale could not be formed.Therefore,only the dense Cr₂O₃ layer protects the matrix effectively in the process of oxidation rather than aluminum oxide.

With the increase of oxidation temperature for 100 h,the diffusion rate of Ti⁴⁺in the alloy speeds up,leading to the rapid growth of TiO₂,and thicker grains of TiO₂ are formed at 900℃than at 800℃.After oxidation at1000℃for 100 h,TiO₂ particles are spalled and then destroy the continuity of the protective Cr₂O₃ film,resulting in the decrease in oxidation resistance of the superalloy [ 15, 16] .

Fig.4 SEM images of surface morphologies of oxidation films after oxidation and corresponding EDS result of oxide scales at a,d 800℃,b,e 900℃and c,f 1000℃

Figure 5a-c show cross-sectional morphologies of GH586 superalloy after oxidation at 800,900 and1000℃for 100 h,Fig.5d-f shows elemental profiles in a cross section with distance from oxidation surface.It is seen from Fig.5a,d that a layer of dense oxide film with3μm in thickness is formed on the surface of superalloy GH586 oxidized at 800℃for 100 h.According to XRD analysis,the oxide film is mainly composed of Cr₂O₃,NiCr₂O₄ and a small amount of TiO₂.Meanwhile,a few aluminum oxides are found at the bottom of the oxidation scales,and a small amount of aluminum-rich oxides(Al₂O₃) exist in the grain boundaries due to the internal oxidation of aluminum,and the depth of the internal oxidation is about 3-4μm.In Fig.5b,e,the thickness of the surface oxide film increases to 10μm after oxidation at 900℃for 100 h,and the film can be pided into two layers.The outer layer with 5μm in thickness becomes looser than the inner,and the depth of the internal oxidation is up to 15-16μm according to the change of aluminum oxides in cross section.In Fig.5c,f,the oxide scale develops into a layer structure after oxidation at1000℃for 100 h.It is seen that aluminum oxides exist at the deeper locations caused by the severer internal oxidation and the depth of the rich-aluminum oxides in the grain boundaries reaches around 40μm.But the thickness of the oxide scale decreases to about 12μm,this is because of the outer oxide film spalled in multiple areas,leading to the great decrease of Ti content in cross section.Meanwhile,the element Cr in substrate diffuses outward to generate a small amount of new Cr₂O₃.Moreover,it is easily seen that Ni content decreases greatly after oxidation at 900℃for 100 h,and it is almost 0 after oxidation at 1000℃for 100 h,as shown in Fig.5d-f,which is caused by the appalling spinels NiCr₂O₄ in oxide scales.

Figure 6 shows EDS results of outer layer,inner layer and internal oxidation region of GH586 superalloy after oxidation at 900℃for 100 h.As shown in Fig.6a,many cracks form in outer layer,which are caused by the large blocks of TiO₂.Through these cracks,oxygen is easily propagated into the matrix and forms aluminum-rich oxides (Al₂O₃) along grain boundaries.Meanwhile,Fig.6b shows that inner layer is a layer of dense Cr₂O₃,including a small amount of TiO₂.The internal oxidation of aluminum beneath the oxide scale is generated along grain boundaries,as its EDS is shown in Fig.6c.Owing to the low aluminum concentration in the alloy,it is not enough to form a continuous oxide film on AI₂O₃.The internal oxide along grain boundaries can help to connect oxide scale at the interface with the matrix,and form a continuous oxide zone at some locations to improve the adhesion of oxide scale effectively [ 17, 18] .

Fig.5 SEM images of cross-sectional morphologies of superalloy for 100 h and corresponding concentration profiles of elements from oxidation surface oxidized at a,d 800℃,b,e 900℃and c,f 1000℃

Fig.6 EDS results of a outer layer,b inner layer and c internal oxidation region at 900℃for 100 h

3.4 Discussion

Figure 7 shows the evolution of oxide scale on superalloy GH586 exposed to air from 800 to 1000℃for 100 h.At the first stage of nucleation,mechanical failure of the initial passive layer might take place,thus leading to the nucleation and growth of initial Cr oxide encountering with O^2-,resulting from the decomposition of oxygen absorbed at the surface of the superalloy.X=0,which is slightly beneath the initial chromium oxide,is the initial surface of the superalloy as the chromium oxide layer grows by countercurrent diffusions of chromium and oxygen.The consistency and integrity of the initial chromium oxide layer depend on the content of the superalloy composition.The slowest kinetic should be attributed to the formation of the chromium oxide layer,which may hinder the diffusion of cations and anions during the first stage of oxidation on the superalloy.Meanwhile,some small titanium oxide particles and Ni-Cr spinels in chromium oxide layer are formed near interface.Owing to the diffusion of only a small amount of oxygen atoms into substrate,the slight internal oxidation along grain boundaries produces a little Al₂O₃.

Owing to that the diffusion rate of Ti⁺⁴ is faster than that of Cr³⁺under the same conditions [ 19] ,titanium oxides (TiO₂) transfer to outer layer of oxide film,and titanium oxides grow up gradually with temperature increasing,resulting in that the outer layer of oxide scale becomes relatively loose at 900℃.It provides the channels for the diffusion of oxygen and accelerates the internal oxidation along grain boundaries.Moreover,the amount and size of Ni-Cr spinels (NiCr₂O₄) in oxide film increase with temperature increasing,and NiCr₂O₄ consumes a part of Cr³⁺diffusing from the matrix,resulting in that the oxidation layer is not able to obtain enough supplement of Cr³⁺ [ 21, 22, 23, 24] .The inner layer of oxidation filmis still compact and integrity,and continues to protect the matrix.At 1000℃,titanium oxides grow into plenty of large blocks which destroy the continuity of the oxide film.The oxide scales in multiple areas are spalled under the action of thermal stress,it may provide the channels for oxygen to diffuse into the matrix,accelerate the oxidation process and reduce the resistance of high temperature oxidation.

The high temperature oxidation resistance of superalloys should be attributed to the chemical compositions of the superalloy,especially the contents of chromium (18-20)wt% [ 25] ,which has been studied quite extensively.When chromium content is higher than 15 wt%,it can form thin composite oxide films mainly containing Cr₂O₃,NiCr₂O₄and TiO₂,which can prevent further oxidation of alloys [ 4] .This evolution process of the oxide film is primarily controlled by ion diffusion [ 26, 27, 28] .Although Cr₂O₃ film prevents the further oxidation of the elements in the alloy,the grown up titanium oxide in the film with temperature and time increasing makes the oxide film more loose;thus it provides channels for oxygen to diffuse into the matrix through oxide film and accelerates the internal oxidation of the superalloy [ 29, 30] .

Fig.7 Oxide scale evolution on surfaces of superalloy GH586 exposure to air from 800 to 1000℃for 100 h

4 Conclusion

The oxidation kinetics curves follow the parabolic law with the activation energy of 241.4 kJ·mol^-1.The oxide scale on the surface of Ni-based superalloy GH586 is composed of Cr₂O₃,NiCr₂O₄ and a small mount of TiO₂.With temperature increasing,TiO₂ particles gradually grow up and destroy the continuity of oxide film.Moreover,the spinels NiCr₂O₄ generated in the process of oxidation greatly consume Cr element in oxide film,which cannot obtain enough supplement of Cr element from the matrix for the oxide scale.At 900℃,the oxide scales display two layer structures:the outer layer of the oxide films consists of Cr₂O₃,NiCr₂O₄ and TiO₂,while the internal oxidation occurs under the oxide film and generates rich-aluminum oxides.At 1000℃for 100 h,the cracks throughout the oxide film accelerate the oxidation rate of Ni-based superalloy GH586.Meanwhile,TiO₂ forms into large blocks and accelerates the oxidation scale spalling.