图书来源:二元合金相图及中间相晶体结构 二元合金相图及中间相晶体结构
作 者:唐仁政 田荣璋
出版时间:2009-05
定 价:320元
图书ISBN:978-7-81105-831-4
出版单位:中南大学出版社
Xiaofeng Wang1), Dazhi Wang1), Cuiwei Do2), Xianghua Kong2), and Qingguo Liu2)1) Department of mechanical engineering, Tsinghua University, Beijing 100084, China2) State Support Laboratory on Solid Electrolytes and Metallurgical Testing Techniques, Univer
摘 要:<正>The fabrication and characterization of new type Nickel oxide/KOH/Active carbon super-capacitor have been described. Porous nickel oxide was prepared by hydrolysis of nickel acetate and heated in air at 300℃. The resulting nickel oxide behaved as an electrochemical capacitor electrode with a specific capacitance (50-70 F/g) superior to most active carbon electrodes. This kind of nickel oxide maintained high utilization at high rate of discharge (i.e., high power density) and had excellent cycle life more than 1 000 times, while the capacitance of the cell composed of two identical nickel oxide electrodes was poor at high discharge current density and the maximum operational voltage of this type capacitor was limited to 0.5 V. A new type super-capacitor was designed in which the nickel oxide and the active carbon were applied to the positive and negative electrodes respectively. The breakdown voltage of this type super-capacitor was improved effectively to 0.8 V and excellent characteristic of high power
关键词: