快速凝固高硅铝合金粉末的热挤压过程

来源期刊:中国有色金属学报2001年第1期

论文作者:张大童 李元元 罗宗强 邱诚

文章页码:6 - 9

关键词:快速凝固; 高硅铝合金; 热挤压

Key words:rapid solidification; hypereutectic Al-Si alloy; hot extrusion

摘    要:通过分析快速凝固高硅铝合金粉末在热挤压过程中的密度、微观组织和相结构的变化,对粉末热挤压成形机理进行了探讨。结果表明,快速凝固高硅铝合金粉末热挤压过程分为2个阶段,即填充挤压阶段和稳态流动阶段,粉末生坯的致密化主要在第一阶段完成。粉末颗粒中初晶Si相受到加热长大和挤压破碎两方面的综合作用,最终得到的挤压材料中的Si颗粒与原始粉末相比没有明显的粗化。合金的相组成在挤压前后没有发生变化,快速凝固合金的组织结构特征基本得以保留。

Abstract: By analyzing the changes of the density, microstructures and phase during the hot extrusion process of rapidly solidified (RS) hypereutectic aluminumsilicon powder, the mechanism of powder hot extrusion was studied. Experimental results show that the powder hot extrusion process can be divided into two stages, hot compress process and stable flow process. The density of the billet increases greatly at the first process. Two effects decide the primary silicon particle size: growing due to heating and breaking due to extrusion. However, no change of phase is detected after hot extrusion, and the powder's RS characteristics remain unchanged.

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号