Structure and Oxidation Behavior of a Plasma Sprayed Yttrium Silicates Coated SiC-C/C with a Glass Outer Sealant from 1573K to 1873K
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2008年第1期
论文作者：黄剑锋
文章页码：33 - 37
摘 要：<正>Different compositions of yttrium silicates coatings were deposited on SiC-C/C by plasma spraying and an outer borosilicate glass was applied on the yttrium silicates coatings surfaces.The structure of the multi-layer coatings was characterized by XRD and SEM analyses.High temperature oxidation behavior of the multi-layer coatings coated C/C composites was investigated.Results show that SiC/2SiO2Y2O3/I.5SiO2 Y2O3/SiO2 Y2O3/glass multi-layer coating has better high temperature oxidation resistance,protecting carbon/ carbon composites from oxidation at 1 773 K in air for 164 h with the weight loss of 1.65%.The oxidation weight loss of the coated C/C with time accorded with parabolic rule in the temperature range 1 573 K-1 873 K; and the corresponding oxidation activation energy of the coated carbon/carbon composites is 132.2 kJ/mol.
黄剑锋
摘 要：<正>Different compositions of yttrium silicates coatings were deposited on SiC-C/C by plasma spraying and an outer borosilicate glass was applied on the yttrium silicates coatings surfaces.The structure of the multi-layer coatings was characterized by XRD and SEM analyses.High temperature oxidation behavior of the multi-layer coatings coated C/C composites was investigated.Results show that SiC/2SiO2Y2O3/I.5SiO2 Y2O3/SiO2 Y2O3/glass multi-layer coating has better high temperature oxidation resistance,protecting carbon/ carbon composites from oxidation at 1 773 K in air for 164 h with the weight loss of 1.65%.The oxidation weight loss of the coated C/C with time accorded with parabolic rule in the temperature range 1 573 K-1 873 K; and the corresponding oxidation activation energy of the coated carbon/carbon composites is 132.2 kJ/mol.
关键词：