DIFFUSION REACTION IN THE INTERFACE OF TITANIUM/MILD STEEL COMPOSITE
来源期刊:中南大学学报(英文版)1996年第2期
论文作者:Yang Yang Zhang Xinming
文章页码:32 - 36
Key words:interface; diffusion reaction; intermetallic compound
Abstract: The microstructure together with the formation and growth of reaction phases in the interfacial diffusion zone of the explosive cladding TA2/A3 has been investigated by means of OM, SEM, AES and XRD techniques. When the specimen annealed at temperature under theβ-Ti→ α-Ti transformation, i. e. below 1173 K, only TiC forms along TA2 side of interface and hinders the interdiffusion of Fe and Ti atoms, thus Fe2Ti or FeTi is unable to occur. While heated up to the transformation temperature ofβ-Ti, e. g, over 1223 K, the parabolic growth of intermetallic compounds of Fe2Ti and FeTi with layer structure may form intergranularly and the formation ofβ-Ti orβ-Ti+α-Ti structure at the Fe enriched side of TA2 and the martensitic transformation products at the Fe-depleted side are observed owing to the diffusion of Fe. Furthermore, the growth ofβ-Ti transformation layer is revealed to follow the parabolic rule