Dy gradient and coercivity in grain boundary diffusion processed Nd-Fe-B magnet
来源期刊：Journal of Rare Earths2017年第6期
论文作者：周磊 李建 程星华 刘涛 喻晓军 李波
文章页码：559 - 566
摘 要：By controlling Dy vapor deposition process, the amount of Dy that diffused into the magnet was increased gradually from 0.1 wt.% to 0.3 wt.%. Compared with the original status, the coercivity increment was not proportional to the Dy diffusion amount. Subsequent Hcj and Dy content gradient data showed that slope of the 0.3 wt.% sample gradient was bigger than that of 0.1 wt.% one, and the gaps between outer flakes and inner flakes enlarged with the increasement of Dy diffusion amount. Although Dy mostly enriched in triple-junction regions in electron-probe microscope analysis（EPMA） images, the following Auger depth graph showed that Dy content was as high as 3.0 at.% in 1.5 mm deep center. It proved that Dy tended to get into the main phase rather than stayed in the grain boundary during the diffusion process, and over-diffusion of Dy in the main phase was unhelpful for the coercivity enhancement.
周磊1，李建1,2，程星华1，刘涛1，喻晓军1，李波2
1. Functional Materials Division, Advanced Technology & Materials Co., Ltd.2. China Iron & Steel Research Institute Group
摘 要：By controlling Dy vapor deposition process, the amount of Dy that diffused into the magnet was increased gradually from 0.1 wt.% to 0.3 wt.%. Compared with the original status, the coercivity increment was not proportional to the Dy diffusion amount. Subsequent Hcj and Dy content gradient data showed that slope of the 0.3 wt.% sample gradient was bigger than that of 0.1 wt.% one, and the gaps between outer flakes and inner flakes enlarged with the increasement of Dy diffusion amount. Although Dy mostly enriched in triple-junction regions in electron-probe microscope analysis（EPMA） images, the following Auger depth graph showed that Dy content was as high as 3.0 at.% in 1.5 mm deep center. It proved that Dy tended to get into the main phase rather than stayed in the grain boundary during the diffusion process, and over-diffusion of Dy in the main phase was unhelpful for the coercivity enhancement.
关键词：