Determination of the Apparent Activation Energy of Concrete Carbonation
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2013年第5期
论文作者：李果 YUAN Yingshu DU Jianmin JI Yongsheng
文章页码：944 - 949
摘 要：Accelerated carbonation experiments about the development of carbonation rates of ordinary Portland cement concrete under different artificial climates were carried out.Six water cement ratios and six climate condition combinations of temperature and relative humidity were used.Results indicate that changes of concrete carbonation rate with environmental temperature agree the Arrhenius law well,which suggests concrete carbonation rate has obvious dependence on temperature.The higher the temperature is,the more quickly the concrete carbonates,and at the same time it is also affected by environmental relative humidity.Thereafter,the apparent activation energy E a of concrete carbonation reaction was obtained,ranging from 16.8 to 20.6 kJ/mol corresponding 0.35-0.74 water cement ratio,and lower water cement ratio will cause the apparent activation energy increase.Concrete carbonation rates will increase 1.1-1.69 times as temperature increase every 10 ℃ at the temperature range of 10 to 60 ℃.
李果，YUAN Yingshu，DU Jianmin，JI Yongsheng
Jiangsu Key Laboratory of Environmental Impact and Structural Safety in Engineering,China University of Mining & Technology
摘 要：Accelerated carbonation experiments about the development of carbonation rates of ordinary Portland cement concrete under different artificial climates were carried out.Six water cement ratios and six climate condition combinations of temperature and relative humidity were used.Results indicate that changes of concrete carbonation rate with environmental temperature agree the Arrhenius law well,which suggests concrete carbonation rate has obvious dependence on temperature.The higher the temperature is,the more quickly the concrete carbonates,and at the same time it is also affected by environmental relative humidity.Thereafter,the apparent activation energy E a of concrete carbonation reaction was obtained,ranging from 16.8 to 20.6 kJ/mol corresponding 0.35-0.74 water cement ratio,and lower water cement ratio will cause the apparent activation energy increase.Concrete carbonation rates will increase 1.1-1.69 times as temperature increase every 10 ℃ at the temperature range of 10 to 60 ℃.
关键词：