来源期刊:中国有色金属学报1997年第1期
论文作者:李凤珍 刘兆晶 金铨 俞泽民
文章页码:98 - 102
关键词:加工软化 回复 轧制率
Key words:pure aluminiums Al-Fe alloys work-softening rolling ratio recovery
摘 要:研究了三种纯度的铝及其 Al-2%Fe合金在室温轧制状态下的加工软化行为及软化机理。试验证明:99.996%Al当轧制率为80%以上时出现加工软化现象;99.96%Al和99.6%Al 不发生加工软化。用99.996%Al配制的 Al-2%Fe 合金当轧制率为60% 以上时出现加工软化;用99.96%Al 配制的Al-2%Fe合金当轧制率为90%以上时出现加工软化;用99.6%Al 配制的Al-2%Fe合金不发生加工软化。室温回复是加工软化的主要原因;Fe有净化铝基体的作用;弥散的第二相有利于室温回复。
Abstract: The work-softening behaviors and mechanisms of three kinds of pure aluminium and three Al-2%Fe alloys in the rolling state at room temperature were studied, the results show that when the rolling ratio is over 80%, there occurs work-softening in the 99.996%Al but not in the 99.96%Al and 99 .6%Al; that there occur work-softening in the Al(99.996%)-2%Fe alloy when the rolling ratio is over 60% and in the Al(99.96%)-2%Fe alloy when the rolling ratio is over 90%, but not in the Al(99.6%)-2%Fe alloy. The main reason of work-softening is room-temperature recovery which is caused by the dispersive second phases.