Microstructure, corrosion and tribological properties of Ti(CN) multilayer coatings on 35CrMo steel by CVD
来源期刊：Rare Metals2020年第11期
论文作者：Jin Zhang Qi Xue Song-Xia Li Zeng Qin
文章页码：1314 - 1320
摘 要：Multilayer hard coatings of TiC/Ti（C,N）/TiN on 35 CrMo steel substrates were deposited by a chemical vapor deposition system（CVD）.X-ray diffraction（XRD）,scanning electron microscopy（SEM）,and energy dispersive X-ray spectrometer（EDX） were used to analyze phase composition,morphology,and chemical composition of the coatings.The mechanical,corrosion,and wear properties of the produced coatings were primarily examined.The results indicate that multilayer coatings are consisted of TiC,Ti(C0.2N0.8),and TiN.The coatings surface is dense,and the thickness is about 11 μm.The adhesion between coatings and steel substrate was characterized by critical load（Lc） and is found to be about 70 N.The microhardness of the multilayer coatings is HV 2400,which is about 5 times as that of the 35 CrMo steel substrate.The corrosion current of the coated sample is 4.368 x10-5 A·cm-2,which decreases by one order of magnitude compared with the uncoated one(1.324 × 10-4 A·cm-2).Friction and wear tests show that the TiC/Ti（C,N）/TiN coatings with high hardness adhere well to the 35 CrMo substrate and display good wear resistance and low friction coefficient under non-lubricated friction test at room temperature.
Jin Zhang，Qi Xue，Song-Xia Li，Zeng Qin
School of Materials Science and Engineering, Southwest Petroleum University
摘 要：Multilayer hard coatings of TiC/Ti（C,N）/TiN on 35 CrMo steel substrates were deposited by a chemical vapor deposition system（CVD）.X-ray diffraction（XRD）,scanning electron microscopy（SEM）,and energy dispersive X-ray spectrometer（EDX） were used to analyze phase composition,morphology,and chemical composition of the coatings.The mechanical,corrosion,and wear properties of the produced coatings were primarily examined.The results indicate that multilayer coatings are consisted of TiC,Ti(C0.2N0.8),and TiN.The coatings surface is dense,and the thickness is about 11 μm.The adhesion between coatings and steel substrate was characterized by critical load（Lc） and is found to be about 70 N.The microhardness of the multilayer coatings is HV 2400,which is about 5 times as that of the 35 CrMo steel substrate.The corrosion current of the coated sample is 4.368 x10-5 A·cm-2,which decreases by one order of magnitude compared with the uncoated one(1.324 × 10-4 A·cm-2).Friction and wear tests show that the TiC/Ti（C,N）/TiN coatings with high hardness adhere well to the 35 CrMo substrate and display good wear resistance and low friction coefficient under non-lubricated friction test at room temperature.
关键词：