Tribological properties of Cu-La2O3 composite under different electrical currents
来源期刊：Journal of Rare Earths2011年第3期
论文作者：郑润国 战再吉 王文魁
文章页码：247 - 252
摘 要：A new type of Cu-La2O3 composite was fabricated by internal oxidation method using powder metallurgy.Sliding wear behavior of the Cu-La2O3 composite was studied on a pin-on-disc wear tester under various electrical currents and applied loads.The worn surfaces were characterized using scanning electron microscopy and energy dispersive spectroscopy to probe the wear mechanisms.The results indicated that applied load had a significant effect on the wear rate of the Cu-La2O3 composite pins.The wear rate displayed the minimum value at the load of 50 N during electrical sliding processes.The corresponding wear mechanism was identified to be adhesive wear,abrasive wear,oxidation wear and arc erosion.
郑润国，战再吉，王文魁
State Key Laboratory of Metastable Materials Science&Technology,School of Science&Technology,Yanshan University
摘 要：A new type of Cu-La2O3 composite was fabricated by internal oxidation method using powder metallurgy.Sliding wear behavior of the Cu-La2O3 composite was studied on a pin-on-disc wear tester under various electrical currents and applied loads.The worn surfaces were characterized using scanning electron microscopy and energy dispersive spectroscopy to probe the wear mechanisms.The results indicated that applied load had a significant effect on the wear rate of the Cu-La2O3 composite pins.The wear rate displayed the minimum value at the load of 50 N during electrical sliding processes.The corresponding wear mechanism was identified to be adhesive wear,abrasive wear,oxidation wear and arc erosion.
关键词：