Effect of Crosslink Structure of Bridge Polycarboxylate Superplasticizers on Dispersion Ability
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2013年第2期
论文作者：毕耀 雷家珩 DU Xiaodi ZHANG Anfu
文章页码：339 - 342
摘 要：Bridge polycarboxylate superplasticizers（PCs） with crosslink structure were synthesized by using polyethyleneglycol di-acrylate（PEGdA）, replacing partial polyethyleneglycol mono-acrylate （PEGmA） as crosslinking agent. Structures of bridge PCs were analyzed by gel permeation chromatography, and dispersion ability was evaluated by cement paste dispersity variation on time and rheology test. The experimental results showed that, molecular weight（MW） of bridge PCs increased with increase of PEGdA proportion, and MW distribution curve changed from Gaussian to flat like, which meant notable increase of highly crosslinked copolymer. Bridge PCs led to decreased initial cement paste dispersity and better dispersity retention due to slow releasing. Further research showed that, PEGdA proportion had slight effect on polymerization degree of backbone, MW distribution of backbone deviated from Gaussian distribution and shoulder peaks appeared on distribution curve when PEGdA increased.
毕耀1，雷家珩1,2，DU Xiaodi2，ZHANG Anfu2
1. School of Materials Science and Engineering, Wuhan University of Technology2. School of Science, Wuhan University of Technology
摘 要：Bridge polycarboxylate superplasticizers（PCs） with crosslink structure were synthesized by using polyethyleneglycol di-acrylate（PEGdA）, replacing partial polyethyleneglycol mono-acrylate （PEGmA） as crosslinking agent. Structures of bridge PCs were analyzed by gel permeation chromatography, and dispersion ability was evaluated by cement paste dispersity variation on time and rheology test. The experimental results showed that, molecular weight（MW） of bridge PCs increased with increase of PEGdA proportion, and MW distribution curve changed from Gaussian to flat like, which meant notable increase of highly crosslinked copolymer. Bridge PCs led to decreased initial cement paste dispersity and better dispersity retention due to slow releasing. Further research showed that, PEGdA proportion had slight effect on polymerization degree of backbone, MW distribution of backbone deviated from Gaussian distribution and shoulder peaks appeared on distribution curve when PEGdA increased.