High-frequency induction heated sintering of ball milled Fe-WC nanocomposites
来源期刊：International Journal of Minerals Metallurgy and Materials2013年第7期
论文作者：T. Zanganeh A. Najafi
文章页码：693 - 699
摘 要：Fe-WC nanocomposites were successfully fabricated by high-frequency induction heated sintering of ball milled nanostructure powders. The ball milled powders were characterized by X-ray diffraction. Density measurements by the Archimedes method show that all sintered samples have the relative density higher than 95%. Studies on the effects of WC content, milling speed, and milling time indicate that a higher milling speed and a more WC content lead to the improvement of mechanical properties. There is a very good distribution of WC particles in the Fe matrix at the milling speed of 650 r/min. For the sintered sample 20-5-650 （20wt% WC, milling time of 5 h, and milled speed of 650 r/min）, the maximum Brinell hardness and yield stress are obtained to be 3.25 GPa and 858 MPa, respectively. All sintered samples have brittle fracture during compression test except the sample 20-5-650.
T. Zanganeh2，A. Najafi2
2. Department of Materials, Saveh Branch, Islamic Azad University, Saveh, Iran
摘 要：Fe-WC nanocomposites were successfully fabricated by high-frequency induction heated sintering of ball milled nanostructure powders. The ball milled powders were characterized by X-ray diffraction. Density measurements by the Archimedes method show that all sintered samples have the relative density higher than 95%. Studies on the effects of WC content, milling speed, and milling time indicate that a higher milling speed and a more WC content lead to the improvement of mechanical properties. There is a very good distribution of WC particles in the Fe matrix at the milling speed of 650 r/min. For the sintered sample 20-5-650 （20wt% WC, milling time of 5 h, and milled speed of 650 r/min）, the maximum Brinell hardness and yield stress are obtained to be 3.25 GPa and 858 MPa, respectively. All sintered samples have brittle fracture during compression test except the sample 20-5-650.
关键词：