Magnetic field stability of PrFeB magnets developed by GBD for cryogenic permanent magnet undulators
来源期刊：JOURNAL OF RARE EARTHS2018年第4期
论文作者：Yongzhou He Xiaoqing Bao Qiaogen Zhou
文章页码：385 - 389
摘 要：The magnetic field stability of the PrFeB magnets is one of the key points which affect its application in such devices as cryogenic permanent magnet undulators. In this study, the magnetic properties and micro structure of PrFeB magnets, which were developed by the grain boundary diffusion, were examined. The demagnetizing field distribution of the cryogenic permanent magnet undulator made using the PrFeB magnets was simulated by Radia, and the change mechanism of the irreversible demagnetization following treatments at high temperatures was experimentally studied, The results show that the intrinsic coercivity of the PrFeB magnets can be increased by diffusion of Tb. Meanwhile, the remanence of the magnets displays almost no loss, and the increasing range is closely related to the orientation thickness of the PrFeB magnet, Therefore, the PrFeB magnets developed using grain boundary diffusion are found to have extremely high comprehensive magnetic properties, The irreversible demagnetization of the PrFeB magnets developed by grain boundary diffusion for the CPMU is determined to be significantly improved following high-temperature treatments.
Yongzhou He1，Xiaoqing Bao2，Qiaogen Zhou1
1. Shanghai Institute of Applied Physics (SINAP)2. University of Science and Technology Beijing (USTB)
摘 要：The magnetic field stability of the PrFeB magnets is one of the key points which affect its application in such devices as cryogenic permanent magnet undulators. In this study, the magnetic properties and micro structure of PrFeB magnets, which were developed by the grain boundary diffusion, were examined. The demagnetizing field distribution of the cryogenic permanent magnet undulator made using the PrFeB magnets was simulated by Radia, and the change mechanism of the irreversible demagnetization following treatments at high temperatures was experimentally studied, The results show that the intrinsic coercivity of the PrFeB magnets can be increased by diffusion of Tb. Meanwhile, the remanence of the magnets displays almost no loss, and the increasing range is closely related to the orientation thickness of the PrFeB magnet, Therefore, the PrFeB magnets developed using grain boundary diffusion are found to have extremely high comprehensive magnetic properties, The irreversible demagnetization of the PrFeB magnets developed by grain boundary diffusion for the CPMU is determined to be significantly improved following high-temperature treatments.
关键词：