TiC-Ni-Mo金属陶瓷的SHS法合成
来源期刊:中国有色金属学报1999年第1期
论文作者:张幸红 赫晓东 王华彬 韩杰才 杜善义
文章页码:106 - 110
关键词:自蔓延高温燃烧合成,金属陶瓷,TiC颗粒,Ni粘结相
Key words:SHS/PHIP, cermet, TiC particles, Ni-binder phase
摘 要:利用自蔓延高温燃烧合成结合准热等静压技术(SHS/PHIP)成功地制备了高致密度的TiC-24Ni-6Mo金属陶瓷(TN30)。 金属陶瓷主要由球形TiC颗粒和近乎网状的Ni粘结相组成。 TiC颗粒与粘结相界面结合良好, 部分粘结相中残留有微量的游离碳。 TN30的抗弯强度和抗压强度分别达到910MPa和3.04GPa。
Abstract: Densified TiC-24Ni-6Mo cermet was prepared by self-propagating high temperature synthesis and pseudo-hot isostatic pressing(SHS/PHIP). The cermet mainly consists of spheroidal TiC particles and quasi-continuous Ni-binder phase. Interfacial bonding between TiC and Ni is found to be of a good quality. Residual C exists in Nia2binder phase. Transverse rupture strength and compressive strength are approximately 910MPa and 3.04GPa, respectively.