Friction and Wear Property of Cu-Cr Alloy
来源期刊：Journal of Rare Earths2007年第S2期
论文作者：刘建华 王玉辉 高红 张瑞军
文章页码：172 - 175
摘 要：The friction and wear behaviors of the Cu-Cr alloy sliding against GCr15 steel at different loads and rotate speed conditions were evaluated, and the worn surface morphologies were observed on a scanning electron microscope. Results show that as loads and rotate speed increase, the wear loss weight increases, by comparison, the biggest friction coefficient of Cu-Cr alloy was obtained at load 100 N and rotate speed at 100 r·min-1 friction condition. Moreover, the dominant wear forms was plough wear.
刘建华，王玉辉，高红，张瑞军
摘 要：The friction and wear behaviors of the Cu-Cr alloy sliding against GCr15 steel at different loads and rotate speed conditions were evaluated, and the worn surface morphologies were observed on a scanning electron microscope. Results show that as loads and rotate speed increase, the wear loss weight increases, by comparison, the biggest friction coefficient of Cu-Cr alloy was obtained at load 100 N and rotate speed at 100 r·min-1 friction condition. Moreover, the dominant wear forms was plough wear.
关键词：