Microstructure and properties in dissimilar/similar weld joints between DP780 and DP980 steels processed by fiber laser welding

来源期刊:JOURNAL OF MATERIALS SCIENCE TECHNOLOG2017年第12期

论文作者:Hongshuang Di Qian Sun Xiaonan Wang Jianping Li

文章页码:1561 - 1571

摘    要:The microstructure and mechanical properties(strength, fatigue and formability) of dissimilar/similar weld joints between DP780 and DP980 steels were studied. The microstructure in fusion zone(FZ) was lath martensite(LM), and alloying elements in the FZ were uniformly distributed. The hardness in the FZ of dissimilar weld joint was similar to the average value(375 HV) of the two similar weld joints. The microstructural evolution in heat affected zone(HAZ) of dissimilar/similar weld joints was as follows:LM(coarse-grained HAZ) →finer LM(fine-grained HAZ) →M-A constituent and ferrite(intercritically HAZ) →tempered martensite(TM) and ferrite(sub-critical HAZ). Lower hardness in intercritically HAZ and sub-critical HAZ(softening zones) was observed compared to base metal(BM) in dissimilar/similar weld joints. The size of softening zone was 0.2–0.3 mm and reduction in hardness was 7.6%–12.7% of BM in all the weld joints, which did not influence the tensile properties of weld joints such that fracture location was in BM. Formability of dissimilar weld joints was inferior compared to similar weld joints because of the softening zone, non-uniform microstructure and hardness on the two sides of FZ. The effect of microstructure on fatigue life was not influenced due to the presence of welding concavity.

详情信息展示

Microstructure and properties in dissimilar/similar weld joints between DP780 and DP980 steels processed by fiber laser welding

Hongshuang Di1,Qian Sun1,Xiaonan Wang2,Jianping Li1

1. State Key Laboratory of Rolling and Automation, Northeastern University2. Shagang School of Iron and Steel, Soochow University

摘 要:The microstructure and mechanical properties(strength, fatigue and formability) of dissimilar/similar weld joints between DP780 and DP980 steels were studied. The microstructure in fusion zone(FZ) was lath martensite(LM), and alloying elements in the FZ were uniformly distributed. The hardness in the FZ of dissimilar weld joint was similar to the average value(375 HV) of the two similar weld joints. The microstructural evolution in heat affected zone(HAZ) of dissimilar/similar weld joints was as follows:LM(coarse-grained HAZ) →finer LM(fine-grained HAZ) →M-A constituent and ferrite(intercritically HAZ) →tempered martensite(TM) and ferrite(sub-critical HAZ). Lower hardness in intercritically HAZ and sub-critical HAZ(softening zones) was observed compared to base metal(BM) in dissimilar/similar weld joints. The size of softening zone was 0.2–0.3 mm and reduction in hardness was 7.6%–12.7% of BM in all the weld joints, which did not influence the tensile properties of weld joints such that fracture location was in BM. Formability of dissimilar weld joints was inferior compared to similar weld joints because of the softening zone, non-uniform microstructure and hardness on the two sides of FZ. The effect of microstructure on fatigue life was not influenced due to the presence of welding concavity.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号