Effects of Sb content on microstructure and mechanical properties of Mg-6Zn-Y-Zr-xSb alloy
来源期刊：中国有色金属学报(英文版)2011年第z2期
论文作者：ZOU Chun-ming ZHANG Yu-min WANG Wei WANG Hong-wei WEI Zun-jie FU Bin-guo
文章页码：222 - 228
Key words：Mg-6Zn-Y-Zr alloy; Sb addition; YSb; Mg3Sb2
Abstract: Effects of Sb content on microstructure and mechanical properties of Mg-6Zn-Y-Zr-xSb alloy were investigated by OM, SEM, XRD and mechanical property test. The results indicate that addition of Sb can break continuous network structure into particles in the interdendritic spaces, and with increasing Sb content, the volume fraction of these particles increases. The as-cast microstructure of the alloy with low content of Sb consists of α-Mg, Zn-rich phase, eutectic structure (α-Mg+I-phase) and YSb. With increasing Sb content, Mg3Sb2 and Mg4Zn7 phases appear, while I-phase disappears finally. The ultimate tensile strength and elongation increase first with the increase of Sb content, while the mechanical properties reduce at excessive Sb content.
ZOU Chun-ming1, 2, 3, ZHANG Yu-min2, WANG Wei1, WANG Hong-wei1, WEI Zun-jie1, FU Bin-guo1
(1. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China;
2. Center for Composite Materials, Harbin Institute of Technology, Harbin 150001, China;
3. Key Laboratory of Bionic Engineering of Ministry of Education, Jilin University, Changchun 130025, China)
Abstract:Effects of Sb content on microstructure and mechanical properties of Mg-6Zn-Y-Zr-xSb alloy were investigated by OM, SEM, XRD and mechanical property test. The results indicate that addition of Sb can break continuous network structure into particles in the interdendritic spaces, and with increasing Sb content, the volume fraction of these particles increases. The as-cast microstructure of the alloy with low content of Sb consists of α-Mg, Zn-rich phase, eutectic structure (α-Mg+I-phase) and YSb. With increasing Sb content, Mg3Sb2 and Mg4Zn7 phases appear, while I-phase disappears finally. The ultimate tensile strength and elongation increase first with the increase of Sb content, while the mechanical properties reduce at excessive Sb content.