简介概要

Glass formation and properties of Ti-based bulk metallic glasses as potential biomaterials with Nb additions

来源期刊：Rare Metals2018年第10期

论文作者：Hui-Ming Yan Ying Liu Shu-Jie Pang Tao Zhang

文章页码：831 - 837

摘要：Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn₂Si₁Ag₂Nb_x （x=0, 1,2; at%） bulk metallic glasses （BMGs） with superior biocorrosion resistance were synthesized by copper mold casting. Although the minor addition of Nb to the Ti-CuZr-Fe-Sn-Si-Ag BMG slightly decreases the glass-forming ability （GF A）, the Nb-bearing Ti-based alloys could be casted in a bulk glassy rod form with diameters up to3 mm. It is found that partial substitution of Cu with Nb is effective on enhancing the bio-corrosion resistance of the Ti-based BMG. Potentiodynamic polarization measurements show that Nb addition to Ti-based BMG leads to higher open-circuit potential and pitting potential as well as lower passive current density in Hank’s solution. Electrochemical impedance spectroscopy （EIS） results indicate that with Nb content increasing, the charge transfer resistance values of the Ti-based BMGs become larger,demonstrating that the surface oxide films are more protective. The Nb-bearing Ti-based BMGs also exhibit good in vitro biocompatibility comparable to that of Ti-6Al-4V alloy. The enhanced bio-corrosion resistance, excellent in vitro biocompatibility and good mechanical properties of the Nb-bearing Ti-based BMGs are favorable for biomedical applications.

稀有金属(英文版) 2018,37(10),831-837

Glass formation and properties of Ti-based bulk metallic glasses as potential biomaterials with Nb additions

Hui-Ming Yan Ying Liu Shu-Jie Pang Tao Zhang

Key Laboratory of Aerospace Materials and Performance(Ministry of Education),School of Materials Science and Engineering, Beihang University

作者简介：*Shu-Jie Pang e-mail: pangshujie@buaa.edu.cn;

收稿日期：24 October 2014

基金：financially supported by the National Natural Science Foundation of China (Nos.51161130526 and 51271008);

Glass formation and properties of Ti-based bulk metallic glasses as potential biomaterials with Nb additions

Hui-Ming Yan Ying Liu Shu-Jie Pang Tao Zhang

Key Laboratory of Aerospace Materials and Performance(Ministry of Education),School of Materials Science and Engineering, Beihang University

Abstract：

Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn₂Si₁Ag₂Nb_x (x=0, 1,2; at%) bulk metallic glasses (BMGs) with superior biocorrosion resistance were synthesized by copper mold casting. Although the minor addition of Nb to the Ti-CuZr-Fe-Sn-Si-Ag BMG slightly decreases the glass-forming ability (GF A), the Nb-bearing Ti-based alloys could be casted in a bulk glassy rod form with diameters up to3 mm. It is found that partial substitution of Cu with Nb is effective on enhancing the bio-corrosion resistance of the Ti-based BMG. Potentiodynamic polarization measurements show that Nb addition to Ti-based BMG leads to higher open-circuit potential and pitting potential as well as lower passive current density in Hank's solution. Electrochemical impedance spectroscopy (EIS) results indicate that with Nb content increasing, the charge transfer resistance values of the Ti-based BMGs become larger,demonstrating that the surface oxide films are more protective. The Nb-bearing Ti-based BMGs also exhibit good in vitro biocompatibility comparable to that of Ti-6Al-4V alloy. The enhanced bio-corrosion resistance, excellent in vitro biocompatibility and good mechanical properties of the Nb-bearing Ti-based BMGs are favorable for biomedical applications.

Keyword：

Ti-based alloy; Bulk metallic glass; Bio-corrosion; Electrochemical impedance spectroscopy; Biocompatibility;

Received： 24 October 2014

1 Introduction

Ti-based bulk metallic glasses (BMGs) with high yield strength,low Young's modulus,high bio-corrosion resistance as well as good formability have potential to be used as biomaterials [ 1, 2, 3, 4, 5, 6, 7, 8, 9] .Considering the biocompatibility,Ti-based BMGs free from highly toxic elements,such as Ni and Be which are the usual constituent components of Tibased alloy for achieving high glass-forming ability,are desired.Recently,Pang et al. [ 4] have succeeded in synthesizing a novel Ni-and Be-free Ti₄₇Cu₃₈Zr_7.5Fe_2.5Sn_2-Si₁Ag₂ BMG with critical diameter up to 7 mm by tilt copper mold casting,and the glassy alloy possesses good mechanical properties,high bio-corrosion resistance and excellent in vitro biocompatibility,demonstrating the application potential as an implant material.Potentiodynamic polarization indicated that the Ti-Cu-Zr-Fe-Sn-SiAg BMG was spontaneously passivated with low passive current density in phosphate-buffered saline (PBS) solution,while pitting corrosion occurred at relatively high potential [ 4] .

It is known that when implanted into human bodies,metallic materials are usually subjected to corrosive processes once they get in touch with the aggressive physiological environment,which comprises amino acids,organic acids,proteins and many inorganic ions such as chlorine [ 10, 11] .Metal ions released from corrodible metal biomaterials to the surrounding tissues in human bodies will cause adverse biological responses,leading to clinical implant failures [ 11] .Meanwhile,the release of ions will also adversely affect the mechanical properties and biocompatibility,thus decreasing the service life of the implanted metallic materials.Therefore,further improving the bio-corrosion resistance,especially the pitting corrosion resistance,is of great importance for the biomedical application of the Ti-Cu-Zr-Fe-Sn-Si-Ag BMG.It has been demonstrated that adding strongly passivating Nb element into Ti-,Zr-and Cu-based BMGs is an effect way to improve the corrosion resistance,especially the pitting corrosion resistance [ 5, 12, 13, 14, 15, 16, 17] .On the other hand,among the constituent elements of the Ti-Cu-Zr-Fe-Sn-Si-Ag BMG,Cu is a relatively unstable element in the solutions containing chloride ions [ 16, 17] .Nb is also recognized as a much more favorable element with respect to Cu from the viewpoint of biocompatibility [ 7] .

Therefore,in this work,addition of Nb to the Ti-Cu-ZrFe-Sn-Si-Ag BMG for replacing partial of Cu was conducted in order to further enhance the bio-corrosion resistance,and the effects of Nb-minor alloying on glassforming ability (GFA),thermal properties,bio-corrosion behaviors in Hank's solution,in vitro biocompatibility and mechanical properties of the Ti-based BMG were investigated.The mechanisms of the glass formation and biocorrosion behavior were also discussed.

2 Experimental

Alloy ingots with nominal compositions of Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn₂Si₁Ag₂Nb_x (x=0,1,2;at%) were prepared from the pure elements by arc melting in a Ti-gettered highpurity argon atmosphere.The mixture of pure Ti and Nb metals was firstly melted to form a pre-alloy and then remelted with the other constituent elements.Ribbon samples and cylindrical rod samples with different diameters were prepared from the master alloys by melt spinning and injection copper mold casting in an argon atmosphere,respectively.Microstructure of the samples was examined by X-ray diffraction (XRD,Bruker AXS D8) using Cu Kαradiation.Thermal behavior of the samples was evaluated using differential scanning calorimeter (DSC,Netzsch 404℃) at a heating rate of0.33 K·s^-1.

Bio-corrosion behaviors of the glassy alloys in Hank's solution at about 310 K were characterized by electrochemical measurements.Prior to the corrosion measurements,the surface of each ribbon sample was mechanically polished with silicon carbide paper up to 2000-grit in cyclohexane,degreased in acetone,washed in distilled water,dried in air and further exposed to air for about 24 h for good reproducibility.For simulating the human body environment,before the electrochemical measurements,the Hank's solution was heated to 310 K with a water bath and aerated with 4 vol%O₂/N₂ mixed gas at a flowing rate of 50 ml·min^-1,which was continued throughout the measurements.Electrochemical measurements were conducted in a three-electrode cell using a platinum counter electrode and a saturated calomel reference electrode(SCE).Potentiodynamic polarization was measured at a potential sweep rate of 0.833×10^-3 V·s^-1 after opencircuit immersion for about 1800 s when the open-circuit potential (OCP) became almost steady.Electrochemical impedance spectroscopy (EIS) measurement was also carried out at the OCP with an alternating current (AC)amplitude of±5 mV in the frequency ranging from1×10^-2 to 1×10⁴ Hz.The impedance data were interpreted on the basis of equivalent circuit,using the ZSimpWin software for fitting the experimental data.For each electrochemical measurement,at least three samples of each alloy were used to confirm the reproducibility.

MC3T3-E1 osteoblast cell line was adopted for preliminary evaluating the in vitro biocompatibility of the Nbbearing Ti-based BMGs in comparison with the Ti-6Al-4V alloy.Cell culture was performed simultaneously on six samples of each alloy.All the samples with a size ofΦ3.0 mm×1.5 mm were mechanically polished with ascending grades of silicon carbide paper up to 2000-grit,followed by polishing to achieve a mirror-like finish.Subsequently,the samples were ultrasonically cleaned in acetone,ethanol and distilled water for 10 min,respectively.Each side of the substrates was sterilized for 1 h by exposure to ultraviolet-visible (UV-Vis) light.MC3T3-E1osteoblast cells were firstly seeded at a cell density of4×10⁴ cell·ml^-1 per well on the prepared substrates in a96-well plate,then cultured in alpha minimum essential medium (α-MEM),and supplemented with 10%fetal bovine serum and 1%antibiotic (penicillin) in a 5 vol%CO₂ balanced air at 310 K.The potential cytotoxicity of the Ti-based BMGs and Ti-6Al-4V alloy was evaluated by3-(4,5-dimethyl-2-thiazolyl)-2,5-diphenyl-2-H-tetrazolium bromide (MTT) assay,and three samples of each alloy were evaluated for reproducibility.After incubation for24 h,the medium was replaced with 100μlα-MEM and25μl MTT in each well and incubated at 310 K for 4 h.The absorbance of the supernatants was measured by a microplate reader at 492 nm.The cell morphology on the remaining three samples of each alloy was observed by scanning electron microscope (SEM,JEOL JSM-6010LA)after cultivating for 24 h.

Compressive mechanical properties of the Ti-based BMGs were evaluated on a material testing machine at a strain rate of 2.0×10^-4 s^-1,and the samples were 2 mm in diameter and 4 mm in length.At least three samples were tested to ensure the repeatability of the results.Morphologies of the deformed samples were observed by scanning electron microscope (SEM).Young's modulus(E) was determined using ultrasound velocity measurement [ 18] .Microhardness of the glassy alloys was measured by Vickers hardness tester under the load of 1.96 N.Densities of the Ti-based alloys were measured by the Archimedean method.

3 Results and discussion

XRD patterns of the as-cast Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn_2-Si₁ Ag₂Nb_x rods with critical diameter of 3 mm prepared by injection copper mold casting are shown in Fig.1.The XRD patterns exhibit a characteristic of board diffraction hump without any distinct crystalline peak,indicating the glassy structure.In previous work,it was found that the Ti₄₇Cu₃₈Zr_7.5Fe_2.5Sn₂Si₁Ag₂ BMG with a diameter of5 mm could be formed by injection copper mold casting.This result indicates that the minor alloying of 1 at%Nb to the Ti-based alloy is slightly detrimental on glass formation,while the addition of more Nb up to 2 at%does not lead to a further reduction in the GFA.DSC curves of Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn₂Si₁Ag₂Nb_x glassy rods with their critical diameters are shown in Fig.2,where T_g and T_xdenote glass transition temperature and the onset temperature of crystallization,respectively.It is seen that the Tibased alloys exhibit the sequential transition of the distinct glass transition,supercooled liquid region and crystallization.The values of T_g,T_x and supercooled liquid region(ΔT_x=T_x—T_g) for the alloys are summarized in Table 1.With Nb content increasing from 0 at%to 2 at%,T_ggradually increases from 640 to 654 K,whereas T_x exhibits no obvious change in the range of 693-695 K,leading to the decrease in supercooled liquid region from 54 to 40 K.The DSC traces of the melt-spun ribbon samples were also examined for comparison,and the result demonstrates that the values of T_g,T_x and heat release of crystallization are nearly identical for the ribbon and the rod samples with the same compositions,which further confirms the amorphous structure of the bulk alloys.The positive mixing heats of Nb-Ti,Nb-Zr and Nb-Cu atomic pairs are 2,4 and3 kJ.mol^-1 [ 19] ,respectively;therefore,the addition of Nb to the Ti-Cu-Zr-Fe-Sn-Si-Ag BMG is unsatisfied with the three empirical compositional rules for achieving a high GFA and contribute to reducing the stability of the supercooled liquid.It was previously reported that repulsive interaction between the atomic pairs due to the positive mixing is thought to induce the formation of less dense random packed structures or atomic clusters,which leads to the easy nucleation and growth reactions of a crystalline phase,a lower viscosity and easier constituent element diffusion [ 20] .Therefore,the addition of Nb into Ti-CuZr-Fe-Sn-Si-Ag BMG deteriorates the thermal stability and GFA.

The corrosion behaviors of Ti₄₇Cu₃₈Zr_7.5Fe_2.5Sn₂Si₁Ag₂BMG in PBS solution were investigated in a former study[4].To further understand the corrosion behaviors of the Ti-Cu-Zr-Fe-Sn-Si-Ag BMG in other artificial body fluids and the effect of Nb addition,a more complex Hank's solution which additionally contains Mg²⁺,Ca²⁺and glucose was adopted in this work.Figure 3 a shows the changes in OCP with immersion time for the Ti-based BMGs in Hank's solution aerated with 4 vol%O₂/N_2.For all alloys,the OCP values rise steeply with immersion time during the initial 50 s and then reach stationary values,implying the formation of stable surface film during the immersion in Hank's solution.It can also be observed that the OCP value slightly increases with the addition of 1 at%Nb and then increases drastically up to about 0.08 V when Nb content reaches 2 at%.This result indicates that the stability of surface film on glassy alloys is enhanced with the increase in Nb content.Potentiodynamic polarization curves of the glassy alloys in Hank's solution open to air at310 K are shown in Fig.3b.It can be seen that the Tibased glassy alloys are spontaneously passivated with a wide passive region and low passive current densities around 0.1 A·m^-2,and pitting corrosion corresponding to the abrupt rise in the current density occurs at relatively high potential.With the Nb content of the Ti-based glassy alloys increasing from 0 at%to 2 at%,the passive current density becomes lower and the pitting potential remarkably increases from 0.90 to 1.21 V.The nobler OCP,higher pitting potential and lower passive current density of the Nb-bearing glassy alloys demonstrate that Nb addition is effective on improving the bio-corrosion resistance of the novel Ti₄₇Cu₃₈Zr_7.5Fe_2.5Sn₂Si₁ Ag₂ BMG in Hank's solution [ 21] ,which is favorable for the biomedical applications.

Fig.1 XRD patterns of Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn₂Si_lAg₂Nb_x BMGs with their critical diameters prepared by injection copper mold casting

Fig.2 DSC curves of Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn₂Si₁Ag₂Nb_x BMGs with their critical diameters

下载原图

Table 1 Thermal stability of Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn₂Si₁ Ag₂Nb_x glassy alloys

Fig.3 Changes in open-circuit potentials (E) with immersion time a and potentiodynamic polarization curves b of Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn_2-Si_iAg2Nb_x BMGs in Hank's solution at 310 K with 4 vol%O₂/N₂

Fig.4 Nyquist diagrams of experimental data and fitted curves of real part (Z') and imaginary part (Z") of impedance and equivalent circuit used in EIS results of interpretation Rs(RctQ) for Ti47Cu38-xZr7.5Fe2.5Sn2Si1Ag2Nbx BMGs in Hank's solution at310 K

Table 2 Values of fitted parameters by equivalent circuit of Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn₂Si₁Ag₂Nb_x_glassy alloys in Hank's solution at310 K with 4 vol%O₂/N₂ aeration 下载原图

Table 2 Values of fitted parameters by equivalent circuit of Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn₂Si₁Ag₂Nb_x_glassy alloys in Hank's solution at310 K with 4 vol%O₂/N₂ aeration

Impedance spectra of Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn₂Si₁Ag₂Nb_xglassy alloys are presented as the Nyquist diagram in Fig.4.It is obvious that the Nyquist diagram of each alloy is characterized by depressed semicircle and only consists of a single capacitance loop.The diameter of the semicircle,depending on the resistance of the passive layer,increases with Nb content,which indicates the enhancement of the corrosion resistance [ 22] .The fitting curves were obtained using the R_s(R_ctQ) model (inset in Fig.4),where R_s denotes the solution resistance,R_ct denotes the charge transfer resistance which reflects the corrosion rate of a metal in solutions [ 23, 24] ,and Q denotes the constant phase element(CPE) instead of pure capacity given the deviations of the system from the ideality due to surface heterogeneities and other possible reasons [ 25] .The impedance of the CPE(ZCPE) is defined by:

where j is imaginary part,ωis angular frequency,Y₀ is admittance constant,and n is the dispersion coefficient.When n=1,the CPE is a capacitor,and when n=0,the CPE is a simple resistor.The fitting parameters of the equivalent circuit are listed in Table 2.It is apparent that the R_ct value of the Ti-based glassy alloys increases with Nb content increasing,which is in accordance with the higher pitting potential and lower passive current density resulted from the increase in Nb content as shown in Fig.3b.It is suggested that Nb could be enriched in the surface oxide films on the Ti-based BMGs containing Nb and depress the diffusion of Cu,leading to the formation of more protective surface film and the higher bio-corrosion resistance [ 12] .

Fig.5 Cytotoxicity of MC3T3-E1 cells cultured on Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn₂Si₁Ag₂Nb_x BMGs and Ti-6Al-4V alloy for 24 h

The result of MTT assay for Ti-Cu-Zr-Fe-Sn-Si-AgNb BMGs is illustrated in Fig.5.It can be seen that the Nbbearing Ti-based BMGs exhibit similar cell viabilities to Ti-6Al-4V alloy,and there is no significant variation in cell viabilities for BMGs with different Nb contents.Figure 6 shows the morphologies of MC3T3-E1 cells after cultivating on Ti-based BMGs and Ti-6Al-4V alloy for24 h.Cells spread extensively on the alloys with polygonal and spindle shapes,and contact with each other through filopodias.This further confirms that the Nb-bearing Tibased BMGs exhibit excellent in vitro biocompatibility compared with Ti-6Al-4V alloy.Good in vitro biocompatibility of Nb-bearing Ti-based BMGs may be attributed to the substitution of Cu with more biocompatible Nb element and the enhanced bio-corrosion resistance which further helps to mitigate the release of constituent elements of the BMGs to the physiological environment.

Fig.7 Compressive stress-strain curves of Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn_2-Si₁Ag₂Nb_x BMGs

Figure 7 shows the compressive stress-strain curves of as-cast glassy alloy rods with diameter of 2 mm.All the Tibased BMGs exhibit large elastic strain of about 2%and subsequent plastic deformation prior to final fracture.Mechanical properties of these Ti-based BMGs are summarized in Table 3.It is seen that with the addition of Nb,there is no obvious change in compressive strength,plastic strain,Young's modulus as well as Vickers hardness,which are around 2000 MPa,2%,98 GPa and HV 590,respectively.SEM observation indicates that the Ti-based BMGs exhibit similar fracture morphology,and the SEM

images of the fractured Ti₄₇Cu₃₆Zr_7.5Fe_2.5Sn₂Si₁Ag₂Nb₂BMG are shown in Fig.8 as representatives.The fracture surface exhibits typical vein-like morphology (Fig.8a),which is characteristic for ductile BMGs [ 26] .As shown in Fig.8b,a number of primary shear bands parallel to the fracture plane and secondary shear bands are formed on the lateral surface of the fractured sample,which contributes to the plasticity of the Ti-based BMGs.Moreover,it is also noted that with Nb content in the Ti-based BMGs increasing from 0 at%to 2 at%,the ratio of Vickers hardness to Young's modulus (HV/E) increases from 0.059to 0.061,which may facilitate good anti-wear performance [ 27, 28] .The high compressive strength,hardness and HV/E values combined with relatively low Young's modulus of the Nb-bearing Ti-based BMGs suggest better mechanocompatibility as biomaterials.

Fig.6 SEM images of MC3T3-E1 cells on cast Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn₂Si₁Ag₂Nb_x (a x=1 and b x=2) BMGs and c Ti-6Al-4V alloy after incubation for 24 h

下载原图

Table 3 Mechanical properties of Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn₂Si₁Ag₂Nb_x BMGs

σy,yielding strength;σf,fracture strength;εp,plastic strain;E,Young's modulus;HV,Vickers microhardness;HV/E,ratio of HV to E

Fig.8 SEM images of Ti₄₇Cu₃₆Zr_7.5Fe_2.5Sn₂Si₁ Ag₂Nb₂ BMG after compressive deformation:a fracture and b lateral surfaces

4 Conclusion

Ti₄₇Cu_38-xZr_7.5Fe_2.5Sn₂Si₁Ag₂Nb_x (x=0,1,2;at%)BMGs with critical diameters up to 3 mm were developed,though the minor addition of Nb to the Ti-Cu-Zr-Fe-SnSi BMG is slightly detrimental to the glass-forming ability.With the increase in Nb content from 0 at%to 2 at%in TiCu-Zr-Fe-Sn-Si-Ag-Nb BMGs,the bio-corrosion resistance in Hank's solution is enhanced,which is indicated by the nobler OCP,higher pitting potential,lower passive current density and larger charge transfer resistance.The improved bio-corrosion resistance with the Nb-alloying is attributed to the formation of more protective surface film,as evidenced by EIS measurement.Excellent biocompatibility of Nb-bearing Ti-based BMGs is revealed by the MTT assay results and cell behaviors.The Nb addition to the Ti-based BMG has no apparent effect on mechanical properties.The combination of enhanced bio-corrosion resistance,good biocompatibility and mechanical properties demonstrates the potential of Ti-based BMGs for use in biomedical applications.