Synthesis and Characterization of Er3+∶Y3Al5O12 Nanocrystalline Powders Prepared by Sol-Gel Method
来源期刊:JOURNAL OF RARE EARTHS2006年增刊第1期
论文作者:Duan Xiulan Wang Lihua Yuan Duorong Shi Xuzhong Li Zhanfa
Key words:preparation; YAG nanocrystalline powders; sol-gel method;
Abstract: Nano-sized Er3+∶Y3Al5O12 powders was successfully prepared via a simple sol-gel route at as low a temperature at 800 ℃ whereas a temperature much higher is necessary to obtain this compound by solid state synthesis (about 1500 ℃). The phase purity, composition and microstructural features of the materials were analyzed by means of X-ray diffraction(XRD), infrared spectroscopy(IR) and transmission electron microscopy(TEM), and no other intermediate phase were observed to form in the range of 700~1000 ℃. The luminescence spectra of Er3+ substituted for Y3+ in YAG in 1% content was characterized on samples at different temperature.
Song Jian'an1,Duan Xiulan1,Wang Lihua1,Yuan Duorong1,Shi Xuzhong1,Li Zhanfa1
(1.State Key Laboratory of Crystal Materials, Shandong University, Jinan 250100, China)
Abstract:Nano-sized Er3+∶Y3Al5O12 powders was successfully prepared via a simple sol-gel route at as low a temperature at 800 ℃ whereas a temperature much higher is necessary to obtain this compound by solid state synthesis (about 1500 ℃). The phase purity, composition and microstructural features of the materials were analyzed by means of X-ray diffraction(XRD), infrared spectroscopy(IR) and transmission electron microscopy(TEM), and no other intermediate phase were observed to form in the range of 700~1000 ℃. The luminescence spectra of Er3+ substituted for Y3+ in YAG in 1% content was characterized on samples at different temperature.