STUDY ON REDUCING THE CORE LOSS OF GRAIN ORIENTED SILICON STEEL AND IMPROVING ITS AGING PROPERTY BY LASER NITRIDING TECHNIQUE IN ATMOSPHERIC AMBIENT
来源期刊:Acta Metallurgica Sinica2005年第4期
论文作者:D.Zhang Y.L Yang C.S.Liu F.J.Sun
Key words:laser nitriding; grain oriented silicon steel sheet; core loss; aging property;
Abstract: CW-CO2 laser nitriding technique was applied to improve the properties (such as aging property and the core loss) of grain oriented silicon steel. The samples were nitrided with regular space.some laser irradiation, Fe4N and Fe3N were formed in the nitrided zone. The nitrided samples were annealed at the temperatures ranged from 100 to 900℃. The core loss of some interested samples was tested. The results show that the core loss of the nitrided samples with different thickness of 0.23 and 0.30mm decreased by 14.9% and 9.4% respectively, and the aging property were improved up to 800℃. The mechanism of laser nitriding to improve the properties of grain oriented silicon steel is discussed.
D.Zhang1,Y.L Yang1,C.S.Liu2,F.J.Sun1
(1.College of Science, Northeastern University, Shenyang 110004, China;
2.College of Material & Metallurgy, Northeastern University, Shenyang 110004,China)
Abstract:CW-CO2 laser nitriding technique was applied to improve the properties (such as aging property and the core loss) of grain oriented silicon steel. The samples were nitrided with regular space.some laser irradiation, Fe4N and Fe3N were formed in the nitrided zone. The nitrided samples were annealed at the temperatures ranged from 100 to 900℃. The core loss of some interested samples was tested. The results show that the core loss of the nitrided samples with different thickness of 0.23 and 0.30mm decreased by 14.9% and 9.4% respectively, and the aging property were improved up to 800℃. The mechanism of laser nitriding to improve the properties of grain oriented silicon steel is discussed.
Key words:laser nitriding; grain oriented silicon steel sheet; core loss; aging property;