Effect of ball milling on hydrogen storage of Mg3La alloy
来源期刊：JOURNAL OF RARE EARTHS2008年第2期
论文作者：SUN Tai ZHU Min DONG Hanwu OUYANG Liuzhang
Key words：hydrogen storage; magnesium based alloys; ball milling; rare earths;
Abstract: Hydrogen storage and microstructure of ball milled Mg3La alloy were investigated by X-ray diffraction and pressure-composition-isotherm measurement. The ball milled Mg3La alloy could absorb hydrogen up to 4wt.% at 300 °C for the first time, along with a decomposing course. Following tests showed that the average reversible hydrogen storage capacity was 2.7wt.%. The enthalpy and entropy of dehydrogenation reaction of the decomposed ball milled Mg3La and hydrogen were calculated. XRD patterns indicated the existence of MgH2 and LaH3 in the decomposed hydride and the formation of Mg when hydrogen was desorbed. After the first hydrogenation, all the latter hydrogenation/dehydrogenation reactions could be taken place between Mg and MgH2. The ball milled Mg3La alloy exhibited better hydriding kinetics than that of the as-cast Mg3La alloy at room temperature. The kinetic curve could be well fitted by Avrami-Erofeev equation.
SUN Tai1，ZHU Min1，DONG Hanwu1，OUYANG Liuzhang1
(1.School of Mechanical Engineering, South China University of Technology, Guangzhou 510641, China)
Abstract:Hydrogen storage and microstructure of ball milled Mg3La alloy were investigated by X-ray diffraction and pressure-composition-isotherm measurement. The ball milled Mg3La alloy could absorb hydrogen up to 4wt.% at 300 °C for the first time, along with a decomposing course. Following tests showed that the average reversible hydrogen storage capacity was 2.7wt.%. The enthalpy and entropy of dehydrogenation reaction of the decomposed ball milled Mg3La and hydrogen were calculated. XRD patterns indicated the existence of MgH2 and LaH3 in the decomposed hydride and the formation of Mg when hydrogen was desorbed. After the first hydrogenation, all the latter hydrogenation/dehydrogenation reactions could be taken place between Mg and MgH2. The ball milled Mg3La alloy exhibited better hydriding kinetics than that of the as-cast Mg3La alloy at room temperature. The kinetic curve could be well fitted by Avrami-Erofeev equation.
Key words:hydrogen storage; magnesium based alloys; ball milling; rare earths;