Microstructure and Properties of Mg-8Li-3Al-1Y Alloy
来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2009年第S1期
论文作者:王威 巫瑞智
文章页码:41 - 43
摘 要:Microstructure of as-cast and extruded Mg-8Li-1Al-1Y alloy specimens was analyzed with OM,SEM and XRD.Results show that as-cast specimens are composed of α phase(Mg),β phase(Li) and rod-like Al2Y compound.In the extruded specimens,the microstructure is refined and the β phase has the effect of coordination during deformation.After extruding process,the Al2Y compound distributes evenly in the extruding direction.The results of mechanical properties tests show that the strength and elongation are both improved after extruding deformation.
王威1,2,巫瑞智1
1. Key Laboratory of Superlight Materials & Surface Technology(Harbin Engineering University),Ministry of Education2. Department of Materials and Chemistry Engineering,Heilongjiang Institute of Technology
摘 要:Microstructure of as-cast and extruded Mg-8Li-1Al-1Y alloy specimens was analyzed with OM,SEM and XRD.Results show that as-cast specimens are composed of α phase(Mg),β phase(Li) and rod-like Al2Y compound.In the extruded specimens,the microstructure is refined and the β phase has the effect of coordination during deformation.After extruding process,the Al2Y compound distributes evenly in the extruding direction.The results of mechanical properties tests show that the strength and elongation are both improved after extruding deformation.
关键词: