Equal Channel Angular Pressing of Tubular Samples
来源期刊：Acta Metallurgica Sinica2013年第5期
论文作者：F.Djavanroodi A.A.Zolfaghari M.Ebrahimi
文章页码：574 - 580
摘 要：A new technique to equal channel angular pressing of tubular samples has been proposed and investigated through experiments and simulations.Deformation behavior of copper tube sample was numerically analyzed during the first pass of tubular ECAP process.The investigation included the efect of various tube wall thicknesses on the efective strain magnitude and strain distribution uniformity.It is shown that tube wall thickness of 3.5 mm gives the optimum value for strain behavior.In addition,copper tube specimens with3.5 mm wall thickness have been successfully ECAPed up to four passes with the die channel angle of 90° using flexible polyurethane rubber pad.Micro-hardness measurements on both annealed and ECAPed tubes show that 33%and 57%increases in hardness value and also,50%and 70%reductions in the grain size were achieved after the first and fourth passes respectively.Furthermore,tube wall thickness measurements show that the process does not change the dimension of deformed specimens.
F.Djavanroodi1,2，A.A.Zolfaghari3，M.Ebrahimi3
1. Department of Mechanical Engineering,Imperial College3. Department of Mechanical Engineering, Iran University of Science and Technology
摘 要：A new technique to equal channel angular pressing of tubular samples has been proposed and investigated through experiments and simulations.Deformation behavior of copper tube sample was numerically analyzed during the first pass of tubular ECAP process.The investigation included the efect of various tube wall thicknesses on the efective strain magnitude and strain distribution uniformity.It is shown that tube wall thickness of 3.5 mm gives the optimum value for strain behavior.In addition,copper tube specimens with3.5 mm wall thickness have been successfully ECAPed up to four passes with the die channel angle of 90° using flexible polyurethane rubber pad.Micro-hardness measurements on both annealed and ECAPed tubes show that 33%and 57%increases in hardness value and also,50%and 70%reductions in the grain size were achieved after the first and fourth passes respectively.Furthermore,tube wall thickness measurements show that the process does not change the dimension of deformed specimens.
关键词：