双温循环热处理对铸态TiAl基合金显微组织的影响

来源期刊：中国有色金属学报1999年第1期

论文作者：彭超群 黄伯云 贺跃辉 孟力平

文章页码：15 - 18

关键词：TiAl基合金，循环热处理,显微组织,晶界形核

Key words：TiAl-based alloy , cyclic heat treatment , microstructure, grain boundary nucleation

摘    要：用Gleeble-1500热模拟机研究了双温循环热处理对铸态TiAl基合金显微组织的影响。 结果表明， 用双温循环热处理可显著细化铸态合金的晶粒尺寸， 最小平均晶粒尺寸可达10μm左右， 且晶粒大小均匀； 新晶粒主要在晶界形核， 并逐步向晶内扩展。 经循环热处理后的样品， 比铸态硬度提高300～900 MPa。

Abstract: The effect of double-temperature cyclic heat treatment on microstructure of a TiAl-based alloy(Ti-33Al-3Cr, mass fraction, %) was studied by means of Gleeble-1500 thermal stimulator. The results showed that the grain size of the as-cast alloy samples can be obviously refined and the smallest average grain size reaches about 10μm, that the nucleations mainly occur at the grain boundaries and propagate into the grains, and that after cyclic heat treatment the HV5 hardness values are raised by 300～900 MPa.