Cyclic oxidation behavior of Fe-9Cr-1Mo steel in water vapor atmosphere
来源期刊：中南大学学报(英文版)2009年第4期
论文作者：张都清 刘光明 赵国群 管延锦
文章页码：535 - 541
Key words：Fe-9Cr-1Mo steel; water vapor; cyclic oxidation; crack
Abstract: The cyclic oxidation behavior of Fe-9Cr-1Mo steel (9Cr-1Mo) in 10%H2O+90%Ar (volume fraction) atmosphere at 600, 650 and 700 ℃ for various time was studied. The oxidation mechanism of 9Cr-1Mo steel in 10%H2O+90%Ar atmosphere was discussed. The thermal stress was evaluated in two oxide layers to illustrate the spallation of the oxide layer. The experimental results indicate that there exists a duplex oxide scale with an outer layer of Fe2O3 and an inner layer of mixed (Fe, Cr)3O4 formed on 9Cr-1Mo steel during cyclic oxidation. Some cracks generated in both inner and outer oxide layers. Parts of oxide scales spalled from substrate during the cyclic oxidation. A higher tensile stress in the oxide layer is formed at the early oxidation stage than at the later oxidation stage during heating. This tensile stress results in the formation of cracks in the oxide layer.
基金信息：the Huadian International Corporation Limited