Effect of precipitation on internal friction of AZ91 magnesium alloy
来源期刊：中国有色金属学报(英文版)2010年增刊第2期
论文作者：刘树伟 姜海昌 李秀艳 戎利建
文章页码：453 - 457
Key words：precipitation; solutionization; isothermal treatment; aging; internal friction
Abstract: The effect of precipitation on the internal friction (IF) of AZ91 magnesium alloy was investigated by using X-ray diffraction (XRD) analysis, scanning electron microscope (SEM) observation, and dynamic mechanical analysis (DMA). Six different states of alloy were prepared by applying different heat treatment processes: as-cast, in-complete solid solution, complete solid solution, micro-precipitation, continuous precipitation and continuous-discontinuous precipitation. It was found that the internal friction of in-completely solid-solutionized, completely solid-solutionized and micro-precipitated specimens showed a similar characteristic, and the grain boundary relaxation is completed depressed due to the Al atoms supersaturated in the α-Mg solution. However, a thermal relaxation internal friction peak was observed for continuously precipitated and continuously- discontinuously precipitated specimens at around 438 K and frequency of about 1 Hz, which was attributed to the grain boundaries relaxation. Furthermore, it was found that the relaxation of the β-Mg17Al12/α-Mg phase interfaces should give its contribution to the background internal friction in the as-cast, continuously precipitated and continuously-discontinuously precipitated specimens.