Microstructure evolution and thixoextrusion of AZ91D magnesium alloy produced by SSTT

来源期刊：中国有色金属学报(英文版)2010年第z3期

论文作者：程远胜 陈强 黄哲群 黄树海

文章页码：739 - 743

Key words：AZ91D magnesium alloy; microstructure; semi-solid thermal transformation; thixoextrusion

Abstract: The semi-solid thermal transformation (SSTT) route was used to obtain semi-solid billets for thixoextrusion. Microstructural evolution during partial remelting was studied. Mechanical properties of thixoextruded billets were determined. The results show that the solid grain size decreases initially and then increases as the isothermal holding time increases. Furthermore, shape factor measurements show that the solid grains tend to become increasingly spheroidal after 10 min isothermal holding. With longer isothermal holding time, the degree of spheroidization slightly decreases. Middle ultimate tensile strength (263.3 MPa) is obtained for thixoextruded AZ91D alloy produced by the SSTT route, with a yield strength of 120.0 MPa and an elongation to fracture of 7.19％.